Multi-layer golf ball

ABSTRACT

Disclosed herein is a multi-layer golf ball having a soft outer cover. The golf ball has an inner cover layer with a Shore D hardness of 60 or more, and an outer cover with a Shore D hardness of 55 or less, and more preferably 50 or less. In a particularly preferred form of the invention, the outer cover comprises one or more polyurethane materials. The golf ball of the invention has exceptionally soft feel and high spin rates on short shots of 80 yards or less, and particularly, 40 yards or less, while maintaining good distance and average spin on full shots.

CROSS REFERENCES TO RELATED APPLICATIONS

The present application is a continuation of U.S. patent applicationSer. No. 11/874,489 filed on Oct. 18, 2007 which is a continuation ofU.S. patent application Ser. No. 11/621,032 filed on Jan. 8, 2007, whichis a continuation of U.S. patent application Ser. No. 10/712,942 filedNov. 23, 2003, now U.S. Pat. No. 7,160,207, which is a divisionalapplication of U.S. application Ser. No. 09/993,422, filed Nov. 5, 2001,now U.S. Pat. No. 6,648,777.

STATEMENT REGARDING FEDERALLY SPONSORED RESEARCH OR DEVELOPMENT

Not Applicable

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to golf balls and, more particularly, toimproved golf balls comprising multi-layer covers which have a hardinner layer and a relatively soft outer layer.

2. Background of the Invention

Traditional golf ball covers have been comprised of balata or blends ofbalata with elastomeric or plastic materials. The traditional balatacovers are relatively soft and flexible. Upon impact, the soft balatacovers compress against the surface of the club producing high spin.Consequently, the soft and flexible balata covers provide an experiencedgolfer with the ability to apply a spin to control the ball in flight inorder to produce a draw or a fade, or a backspin which causes the ballto ‘bite’ or stop abruptly on contact with the green. Moreover the softbalata covers produce a soft “feel” to the low handicap player. Suchplayability properties (workability, feel, etc.) are particularlyimportant in short iron play with low swing speeds and are exploitedsignificantly by relatively skilled players.

Despite all the benefits of balata, balata covered golf balls are easilycut and/or damaged if mis-hit. Golf balls produced with balata orbalata-containing cover compositions therefore have a relatively shortlife-span.

As a result of this negative property, balata and its syntheticsubstitutes, trans-polybutadiene and transpolyisoprene, have beenessentially replaced as the cover materials of choice by new covermaterials comprising ionomeric resins.

Ionomeric resins are polymers containing interchain ionic bonding. As aresult of their toughness, durability and flight characteristics,various ionomeric resins sold by E.I. DuPont de Nemours & Company underthe trademark “Surlyn®” and more recently, by the Exxon Corporation (seeU.S. Pat. No. 4,911,451) under the trademarks “Escor®” and thedesignation Iotek®, have become the materials of choice for theconstruction of golf ball covers over the traditional “balata”(transpolyisoprene, natural or synthetic) rubbers. As stated, the softerbalata covers, although exhibiting enhanced playability properties, lackthe durability (cut and abrasion resistance, fatigue endurance, etc.)properties required for repetitive play.

Ionomeric resins are generally ionic copolymers of an olefin, such asethylene, and a metal salt of an unsaturated carboxylic acid, such asacrylic acid, methacrylic acid, or maleic acid. Metal ions, such assodium or zinc, are used to neutralize some portion of the acidic groupin the copolymer resulting in a thermoplastic elastomer exhibitingenhanced properties, i.e. durability, etc., for golf ball coverconstruction over balata. However, some of the advantages gained inincreased durability have been offset to some degree by the decreasesproduced in playability. This is because although the ionomeric resinsare very durable, they tend to be very hard when utilized for golf ballcover construction, and thus lack the degree of softness required toimpart the spin necessary to control the ball in flight. Since theionomeric resins are harder than balata, the ionomeric resin covers donot compress as much against the face of the club upon impact, therebyproducing less spin. In addition, the harder and more durable ionomericresins lack the “feel” characteristic associated with the softer balatarelated covers.

As a result, while there are currently more than fifty (50) commercialgrades of ionomers available both from DuPont and Exxon, with a widerange of properties which vary according to the type and amount of metalcations, molecular weight, composition of the base resin (i.e., relativecontent of ethylene and methacrylic and/or acrylic acid groups) andadditive ingredients such as reinforcement agents, etc., a great deal ofresearch continues in order to develop a golf ball cover compositionexhibiting not only the improved impact resistance and carrying distanceproperties produced by the “hard” ionomeric resins, but also theplayability (i.e., “spin”, “feel”, etc.) characteristics previouslyassociated with the “soft” balata covers, properties which are stilldesired by the more skilled golfer.

Consequently, a number of two-piece (a solid resilient center or corewith a molded cover) and three-piece (a liquid or solid center,elastomeric winding about the center, and a molded cover) golf ballshave been produced to address these needs. The different types ofmaterials utilized to formulate the cores, covers, etc. of these ballsdramatically alters the balls' overall characteristics. In addition,multi-layered covers containing one or more ionomer resins have alsobeen formulated in an attempt to produce a golf ball having the overalldistance, playability and durability characteristics desired.

This was addressed by Spalding Sports Worldwide, Inc., the assignee ofthe present invention, in U.S. Pat. No. 4,431,193 where a multi-layeredgolf ball is produced by initially molding a first cover layer on aspherical core and then adding a second layer. The first layer iscomprised of a hard, high flexural modulus resinous material such astype 1605 Surlyn® (now designated Surlyn® 8940). Type 1605 Surlyn®(Surlyn® 8940) is a sodium ion based low acid (less than or equal to 15weight percent methacrylic acid) ionomer resin having a flexural modulusof about 51,000 psi. An outer layer of a comparatively soft, lowflexural modulus resinous material such as type 1855 Surlyn® (nowdesignated Surlyn® 9020) is molded over the inner cover layer. Type 1855Surlyn® (Surlyn® 9020) is a zinc ion based low acid (10 weight percentmethacrylic acid) ionomer resin having a flexural modulus of about14,000 psi.

The '193 patent teaches that the hard, high flexural modulus resin whichcomprises the first layer provides for a gain in coefficient ofrestitution over the coefficient of restitution of the core. Theincrease in the coefficient of restitution provides a ball which servesto attain or approach the maximum initial velocity limit of 255 feet persecond as provided by the United States Golf Association (U.S.G.A.)rules. The relatively soft, low flexural modulus outer layer providesfor the advantageous “feel” and playing characteristics of a balatacovered golf ball.

In various attempts to produce a durable, high spin ionomer golf ball,the golfing industry has blended the hard ionomer resins with a numberof softer ionomeric resins. U.S. Pat. Nos. 4,884,814 and 5,120,791 aredirected to cover compositions containing blends of hard and softionomeric resins. The hard copolymers typically are made from an olefinand an unsaturated carboxylic acid. The soft copolymers are generallymade from an olefin, an unsaturated carboxylic acid, and an acrylateester. It has been found that golf ball covers formed from hard-softionomer blends tend to become scuffed more readily than covers made ofhard ionomer alone. It would be useful to develop a golf ball having acombination of softness and durability which is better than thesoftness-durability combination of a golf ball cover made from ahard-soft ionomer blend.

Most professional golfers and good amateur golfers desire a golf ballthat provides distance when hit off a driver, control and stoppingability on full iron shots, and high spin on short “touch and feel”shots. Many conventional two-piece and thread wound performance golfballs have undesirable high spin rates on full shots. The excessive spinon full shots is a sacrifice made in order to achieve more spin which isdesired on the shorter touch shots. It would be beneficial to provide agolf ball which has high spin for touch shots without generatingexcessive spin on full shots.

SUMMARY OF THE INVENTION

An object of the invention is to provide a golf ball with a soft coverwhich has good scuff resistance.

Yet another object of the invention is to provide a golf ball having afavorable combination of spin rate and durability.

A further object of the invention is to provide a golf ball having asoft cover made from a cover material which is blended with minimalmixing difficulties.

Another object of the invention is to provide a method of making a golfball which has a soft cover with good scuff resistance and cutresistance.

Another object of the invention is to provide a golf ball which has ahigh spin on shots of 250 feet or less and an average spin on full shotsusing a 9 iron.

Yet another object of the invention is to provide a method of making adurable golf ball with a relatively high spin rate.

A further object of the invention is to provide a multi-layer golf ballhaving exceptionally soft feel and high spin rates on short shots whilemaintaining good distance on full shots.

Yet another object of the invention is to provide a multi-layer golfball having a high spin rate on short shots and not having an excessivespin rate on long shots.

Other objects will be in part obvious and in part pointed out more indetail hereafter.

In a first aspect, the present invention provides a golf ball,comprising a core, a thermoplastic inner cover layer formed over thecore, the inner cover layer having a Shore D hardness of at least 60 asmeasured on the surface thereof, and an outer cover layer formed overthe inner cover layer, the outer cover layer having a Shore D hardnessof no more than 55 as measured on the surface thereof, the golf ballhaving a PGA compression of 100 or less and a coefficient of restitutionof at least 0.770.

In another aspect, the present invention provides a golf ball comprisinga core, an inner cover layer formed over the core, and an outer coverlayer formed over the inner cover layer. The inner cover layer has aShore D hardness of at least 60 as measured on the curved surfacethereof and is formed of a composition including at least one materialselected from the group of consisting of polyphenylene ether/ionomerblends, ionomers, polyamides, polyurethanes, polyester elastomers,polyester amides, metallocene catalyzed polyolefins, and blends thereof.The outer cover layer has a Shore D hardness of no more than 55 asmeasured on the curved surface thereof. The golf ball has a spin factorof about 5, a PGA compression of 100 or less, and a coefficient ofrestitution of at least 0.770.

In yet another aspect, the present invention provides a golf ballcomprising an inner ball and an outer cover layer formed over the innerball. The inner ball comprises a core and an inner cover layer disposedabout the core. The inner ball has a coefficient of restitution of atleast 0.780. The outer cover layer has a Shore D hardness of no morethan 55 as measured on the curved surface thereof. The golf ball has acoefficient of restitution of at least 0.770 and a PGA compression of100 or less.

In a further aspect, the present invention provides a golf ballcomprising a core, an inner cover layer disposed about the core, and anouter cover layer disposed about the inner cover layer. The inner coverlayer has a Shore D hardness of at least 60 as measured on the curvedsurface thereof and comprises at least one material selected from thegroup consisting of polyphenylene ether/ionomer blends, ionomers,polyamides, polyurethanes, polyester elastomers, polyester amides,metallocene catalyzed polyolefins, and blends thereof. The outer coverlayer has a Shore D hardness of no more than 55 as measured on thecurved surface thereof and comprises at least one material selected fromthe group consisting of polyphenylene ether/ionomer blends, ionomers,polyamides, polyurethanes, polyester elastomers, polyester amides,metallocene catalyzed polyolefins, and blends thereof. The golf ball hasa PGA compression of 100 or less and a coefficient of restitution of atleast 0.770.

The invention accordingly comprises the several steps and the relationof one or more of such steps with respect to each of the others and thearticles possessing the features, properties, and the relation ofelements exemplified in the following detailed disclosure.

BRIEF DESCRIPTION OF THE DRAWINGS

The following is a brief description of the drawings, which arepresented for the purposes of illustrating the invention and not for thepurposes of limiting the same.

FIG. 1 is a cross-sectional view of a golf ball embodying the inventionillustrating a core 10 and a cover 12 consisting of an inner layer 14and an outer layer 16 having dimples 18; and

FIG. 2 is a diametrical cross-sectional view of a golf ball of theinvention having a core 10 and a cover 12 made of an inner layer 14 andan outer layer 16 having dimples 18.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention relates to improved multi-layer golf balls,particularly a golf ball comprising a multi-layered cover 12 over asolid core 10, and method for making same. The golf balls of theinvention, which can be of a standard or enlarged size, have a uniquecombination of high coefficient of restitution and a high spin rate onshort shots.

The core 10 of the golf ball can be formed of a solid, a liquid, or anyother substance which will result in an inner ball, i.e. core and innercover layer, having the desired COR, compression and hardness. Themulti-layered cover 12 comprises two layers: a first or inner layer orply 14 and a second or outer layer or ply 16. The inner layer 14 can beionomer, ionomer blends, non-ionomer, non-ionomer blends, or blends ofionomer and non-ionomer. The outer layer 16 is softer than the innerlayer and can be ionomer, ionomer blends, non-ionomer, non-ionomerblends or blends of ionomer and non-ionomer.

In a first preferred embodiment, the inner layer 14 is comprised of ahigh acid (i.e. greater than 16 weight percent acid) ionomer resin orhigh acid ionomer blend. Preferably, the inner layer is comprised of ablend of two or more high acid (i.e. at least 16 weight percent acid)ionomer resins neutralized to various extents by different metalcations. The inner cover layer may or may not include a metal stearate(e.g., zinc stearate) or other metal fatty acid salt. The purpose of themetal stearate or other metal fatty acid salt is to lower the cost ofproduction without affecting the overall performance of the finishedgolf ball. In a second embodiment, the inner layer 14 is comprised of alow acid (i.e. 16 weight percent acid or less) ionomer blend.Preferably, the inner layer is comprised of a blend of two or more lowacid (i.e. 16 weight percent acid or less) ionomer resins neutralized tovarious extents by different metal cations. The inner cover layer may ormay not include a metal stearate (e.g., zinc stearate) or other metalfatty acid salt.

It has been found that a hard inner layer provides for a substantialincrease in resilience (i.e., enhanced distance) over known multi-layercovered balls. The softer outer layer provides for desirable “feel” andhigh spin rate while maintaining respectable resiliency. The soft outerlayer allows the cover to deform more during impact and increases thearea of contact between the club face and the cover, thereby impartingmore spin on the ball. As a result, the soft cover provides the ballwith a balata-like feel and playability characteristics with improveddistance and durability. Consequently, the overall combination of theinner and outer cover layers results in a golf ball having enhancedresilience (improved travel distance) and durability (i.e. cutresistance, etc.) characteristics while maintaining and in manyinstances, improving, the playability properties of the ball.

The combination of a hard inner cover layer with a soft, relatively lowmodulus ionomer, ionomer blend or other non-ionomeric thermoplasticelastomer outer cover layer provides for excellent overall coefficientof restitution (i.e., excellent resilience) because of the improvedresiliency produced by the inner cover layer. While some improvement inresiliency is also produced by the outer cover layer, the outer coverlayer generally provides for a more desirable feel and high spin,particularly at lower swing speeds with highly lofted clubs such as halfwedge shots.

Inner Cover Layer

The inner cover layer is harder than the outer cover layer and generallyhas a thickness in the range of 0.01 to 0.15 inches, preferably0.01-0.10 inches, more preferably 0.03 to 0.07 inches for a 1.68 inchball and 0.05 to 0.10 inches for a 1.72 inch (or more) ball. The coreand inner cover layer together form an inner ball having a coefficientof restitution of 0.780 or more and more preferably 0.790 or more, and adiameter in the range of 1.48-1.66 inches for a 1.68 inch ball and1.50-1.70 inches for a 1.72 inch (or more) ball. The inner cover layerhas a Shore D hardness of 60 or more. It is particularly advantageous ifthe golf balls of the invention have an inner layer with a Shore Dhardness of 65 or more. The above-described characteristics of the innercover layer provide an inner ball having a PGA compression of 100 orless. It is found that when the inner ball has a PGA compression of 90or less, excellent playability results.

The inner layer compositions of the embodiments described herein mayinclude the high acid ionomers such as those developed by E.I. DuPont deNemours & Company under the trademark Surlyn® and by Exxon Corporationunder the trademark Escor® or tradename Iotek®, or blends thereof.Examples of compositions which may be used as the inner layer herein areset forth in detail in U.S. Ser. No. 08/174,765, now abandoned, which isa continuation of U.S. Ser. No. 07/776,803 filed Oct. 15, 1991, nowabandoned, and Ser. No. 08/493,089, issued as U.S. Pat. No. 5,688,869,which is a continuation of Ser. No. 07/981,751, now abandoned, which inturn is a continuation of Ser. No. 07/901,660 filed Jun. 19, 1992, nowabandoned, all of which are incorporated herein by reference. Of course,the inner layer high acid ionomer compositions are not limited in anyway to those compositions set forth in said copending applications.

The high acid ionomers which may be suitable for use in formulating theinner layer compositions of the subject invention are ionic copolymerswhich are the metal, i.e., sodium, zinc, magnesium, etc., salts of thereaction product of an olefin having from about 2 to 8 carbon atoms andan unsaturated monocarboxylic acid having from about 3 to 8 carbonatoms. Preferably, the ionomeric resins are copolymers of ethylene andeither acrylic or methacrylic acid. In some circumstances, an additionalcomonomer such as an acrylate ester (i.e., iso- or n-butylacrylate,etc.) can also be included to produce a softer terpolymer. Thecarboxylic acid groups of the copolymer are partially neutralized (i.e.,approximately 10-100%, preferably 30-70%) by the metal ions. Each of thehigh acid ionomer resins which may be included in the inner layer covercompositions of the invention contains greater than about 16% by weightof a carboxylic acid, preferably from about 17% to about 25% by weightof a carboxylic acid, more preferably from about 18.5% to about 21.5% byweight of a carboxylic acid.

Although the inner layer cover composition preferably includes a highacid ionomeric resin and the scope of the patent embraces all known highacid ionomeric resins falling within the parameters set forth above,only a relatively limited number of these high acid ionomeric resinshave recently become commercially available.

The high acid ionomeric resins available from Exxon under thedesignation Escor® and or Iotek®, are somewhat similar to the high acidionomeric resins available under the Surlyn® trademark. However, sincethe Escor®/Iotek® ionomeric resins are sodium or zinc salts ofpoly(ethylene-acrylic acid) and the Surlyn® resins are zinc, sodium,magnesium, etc. salts of poly(ethylene-methacrylic acid), distinctdifferences in properties exist.

Examples of the high acid methacrylic acid based ionomers found suitablefor use in accordance with this invention include Surlyn® 8220 and 8240(both formerly known as forms of Surlyn® AD-8422), Surlyn® 9220 (zinccation), Surlyn® SEP-503-1 (zinc cation), and Surlyn® SEP-503-2(magnesium cation). According to DuPont, all of these ionomers containfrom about 18.5 to about 21.5% by weight methacrylic acid.

More particularly, Surlyn® AD-8422 is currently commercially availablefrom DuPont in a number of different grades (i.e., AD-8422-2, AD-8422-3,AD-8422-5, etc.) based upon differences in melt index. According toDuPont, Surlyn® 8422, which is believed recently to have beenredesignated as 8220 and 8240, offers the following general propertieswhen compared to Surlyn® 8920, the stiffest, hardest of all on the lowacid grades (referred to as “hard” ionomers in U.S. Pat. No. 4,884,814):

TABLE 1 LOW ACID HIGH ACID (15 wt % Acid) (>20 wt % Acid) SURLYN ®SURLYN ® SURLYN ® 8920 8422-2 8422-3 IONOMER Cation Na Na Na Melt Index1.2 2.8 1.0 Sodium, Wt % 2.3 1.9 2.4 Base Resin MI 60 60 60 MP¹, ° C. 8886 85 FP¹, ° C. 47 48.5 45 COMPRESSION MOLDING² Tensile Break (psi) 43504190 5330 Yield (psi) 2880 3670 3590 Elongation (%) 315 263 289 FlexModulus (Kpsi) 53.2 76.4 88.3 Shore D Hardness 66 67 68 ¹DSC secondheat, 10° C./min heating rate. ²Samples Compression molded at 150° C.annealed 24 hours at 60° C. 8422-2, -3 were homogenized at 190° C.before molding.

In comparing Surlyn® 8920 to Surlyn® 8422-2 and Surlyn® 8422-3, it isnoted that the high acid Surlyn® 8422-2 and 8422-3 ionomers have ahigher tensile yield, lower elongation, slightly higher Shore D hardnessand much higher flexural modulus. Surlyn® 8920 contains 15 weightpercent methacrylic acid and is 59% neutralized with sodium.

In addition, Surlyn® SEP-503-1 (zinc cation) and Surlyn® SEP-503-2(magnesium cation) are high acid zinc and magnesium versions of theSurlyn® AD 8422 high acid ionomers. When compared to the Surlyn® AD 8422high acid ionomers, the Surlyn SEP-503-1 and SEP-503-2 ionomers can bedefined as follows:

Surlyn ® Ionomer Ion Melt Index Neutralization % AD 8422-3 Na 1.0 45 SEP503-1 Zn 0.8 38 SEP 503-2 Mg 1.8 43

Furthermore, Surlyn® 8162 is a zinc cation ionomer resin containingapproximately 20% by weight (i.e. 18.5-21.5% weight) methacrylic acidcopolymer that has been 30-70% neutralized, Surlyn® 8162 is currentlycommercially available from DuPont.

Examples of the high acid acrylic acid based ionomers suitable for usein the present invention also include the Escor® or Iotek® high acidethylene acrylic acid ionomers produced by Exxon such as Ex 1001, 1002,959, 960, 989, 990, 1003, 1004, 993, 994. In this regard, Escor® orIotek® 959 is a sodium ion neutralized ethylene-acrylic neutralizedethylene-acrylic acid copolymer. According to Exxon, Ioteks® 959 and 960contain from about 19.0 to about 21.0% by weight acrylic acid withapproximately 30 to about 70 percent of the acid groups neutralized withsodium and zinc ions, respectively. The physical properties of thesehigh acid acrylic acid based ionomers are as follows:

TABLE 2 Exxon High Acid Ionomers ESCOR ® ESCOR ® (IOTEK) (IOTEK)Property Ex 1001 Ex 1002 959 Ex 1003 Ex 1004 960 Melt index, g/10 min.1.0 1.6 2.1 1.1 2.0 1.8 Cation Na Na Na Zn Zn Zn Melting Point, ° C.83.7 83.7 — 82 82.5 79 Vicat Softening 51.5 51.5 58 56 55 55 Point, ° C.Tensile @ Break 34.4 MPa 31.7 MPa  34 MPa 24.8 MPa 20.6 MPa  24 MPaElongation @ Break, % 341 348 280 387 437 430 Hardness, Shore D 63 62 6554 53 57 Flexural Modulus  365 MPa  380 MPa 480 MPa  147 MPa  130 MPa170 MPa

TABLE 3 Additional Exxon High Acid Ionomers Property Unit EX 989 EX 993EX 994 EX 990 Melt Index g/10 min. 1.30 1.25 1.32 1.24 Moisture ppm 482214 997 654 Cation Type — Na Li K Zn M+ content by AAS wt % 2.74 0.874.54 0 Zn content by AAS wt % 0 0 0 3.16 Density kg/m³ 959 945 976 977Vicat softening point ° C. 52.5 51 50 55.0 Crystallization point ° C.40.1 39.8 44.9 54.4 Melting point ° C. 82.6 81.0 80.4 81.0 Tensile atyield MPa 23.8 24.6 22 16.5 Tensile at break MPa 32.3 31.1 29.7 23.8Elongation at break % 330 260 340 357 1% secant modulus MPa 389 379 312205 Flexural modulus MPa 340 368 303 183 Abrasion resistance mg 20.0 9.215.2 20.5 Hardness Shore D — 62 62.5 61 56 Zwick Rebound % 61 63 59 48

Furthermore, as a result of the development by the assignee of thisapplication of a number of new high acid ionomers neutralized to variousextents by several different types of metal cations, such as bymanganese, lithium, potassium, calcium and nickel cations, several newhigh acid ionomers and/or high acid ionomer blends besides sodium, zincand magnesium high acid ionomers or ionomer blends are now available forgolf ball cover production. It has been found that these new cationneutralized high acid ionomer blends produce inner cover layercompositions exhibiting enhanced hardness and resilience due tosynergies which occur during processing. Consequently, the metal cationneutralized high acid ionomer resins recently produced can be blended toproduce substantially higher C.O.R.'s than those produced by the lowacid ionomer inner cover compositions presently commercially available.

More particularly, several new metal cation neutralized high acidionomer resins have been produced by the inventor by neutralizing, tovarious extents, high acid copolymers of an alpha-olefin and an alpha,beta-unsaturated carboxylic acid with a wide variety of different metalcation salts. This discovery is the subject matter of U.S. applicationSer. No. 08/493,089, now U.S. Pat. No. 5,688,869, incorporated herein byreference. It has been found that numerous new metal cation neutralizedhigh acid ionomer resins can be obtained by reacting a high acidcopolymer (i.e. a copolymer containing greater than 16% by weight acid,preferably from about 17 to about 25 weight percent acid, and morepreferably about 20 weight percent acid), with a metal cation saltcapable of ionizing or neutralizing the copolymer to the extent desired(i.e. from about 10% to 90%).

The base copolymer is made up of greater than 16% by weight of an alpha,beta-unsaturated carboxylic acid and an alpha-olefin. Optionally, asoftening comonomer can be included in the copolymer. Generally, thealpha-olefin has from 2 to 10 carbon atoms and is preferably ethylene,and the unsaturated carboxylic acid is a carboxylic acid having fromabout 3 to 8 carbons. Examples of such acids include acrylic acid,methacrylic acid, ethacrylic acid, chloroacrylic acid, crotonic acid,maleic acid, fumaric acid, and itaconic acid, with acrylic acid beingpreferred.

The softening comonomer that can be optionally included in the innercover layer for the golf ball of the invention may be selected from thegroup consisting of vinyl esters of aliphatic carboxylic acids whereinthe acids have 2 to 10 carbon atoms, vinyl ethers wherein the alkylgroups contains 1 to 10 carbon atoms, and alkyl acrylates ormethacrylates wherein the alkyl group contains 1 to 10 carbon atoms.Suitable softening comonomers include vinyl acetate, methyl acrylate,methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate,butyl methacrylate, or the like.

Consequently, examples of a number of copolymers suitable for use toproduce the high acid ionomers included in the present inventioninclude, but are not limited to, high acid embodiments of anethylene/acrylic acid copolymer, an ethylene/methacrylic acid copolymer,an ethylene/itaconic acid copolymer, an ethylene/maleic acid copolymer,an ethylene/methacrylic acid/vinyl acetate copolymer, anethylene/acrylic acid/vinyl alcohol copolymer, etc. The base copolymerbroadly contains greater than 16% by weight unsaturated carboxylic acid,from about 39 to about 83% by weight ethylene and from 0 to about 40% byweight of a softening comonomer. Preferably, the copolymer containsabout 20% by weight unsaturated carboxylic acid and about 80% by weightethylene. Most preferably, the copolymer contains about 20% acrylic acidwith the remainder being ethylene.

Along these lines, examples of the preferred high acid base copolymerswhich fulfill the criteria set forth above, are a series ofethylene-acrylic copolymers which are commercially available from TheDow Chemical Company, Midland, Mich., under the Primacor® designation.These high acid base copolymers exhibit the typical properties set forthbelow in Table 4.

TABLE 4 Typical Properties of Primacor Ethylene-Acrylic Acid CopolymersVICAT TENSILE FLEXURAL SOFT SHORE D DENSITY MELT YD ST G/10 MODULUS PTHARDNESS GRADE PERCENT G/CC INDEX MIN (PSI) (° PSI) (° C.) ASTM ACIDD-792 D-1238* D-630 D-790 D-1525 D-2240 5980 20.0 0.958 300.0 — 4800 4350 5990 20.0 0.955 1300.0 650 40 42 5981 20.0 0.960 300.0 900 3200 46 485983 20.0 0.958 500.0 850 3100 44 45 5991 20.0 0.953 2600.0 635 2600 3840 *190° C.Due to the high molecular weight of the Primacor® 5981 grade of theethylene-acrylic acid copolymer, this copolymer is the more preferredgrade utilized in the invention.

The metal cation salts utilized in the invention are those salts whichprovide the metal cations capable of neutralizing, to various extents,the carboxylic acid groups of the high acid copolymer. These includeacetate, oxide or hydroxide salts of lithium, calcium, zinc, sodium,potassium, nickel, magnesium, and manganese.

Examples of such lithium ion sources are lithium hydroxide monohydrate,lithium hydroxide, lithium oxide and lithium acetate. Sources for thecalcium ion include calcium hydroxide, calcium acetate and calciumoxide. Suitable zinc ion sources are zinc acetate dihydrate and zincacetate, a blend of zinc oxide and acetic acid. Examples of sodium ionsources are sodium hydroxide and sodium acetate. Sources for thepotassium ion include potassium hydroxide and potassium acetate.Suitable nickel ion sources are nickel acetate, nickel oxide and nickelhydroxide. Sources of magnesium include magnesium oxide, magnesiumhydroxide, magnesium acetate. Sources of manganese include manganeseacetate and manganese oxide.

The new metal cation neutralized high acid ionomer resins are producedby reacting the high acid base copolymer with various amounts of themetal cation salts above the crystalline melting point of the copolymer,such as at a temperature from about 200° F. to about 500° F., preferablyfrom about 250° F. to about 350° F. under high shear conditions at apressure of from about 10 psi to 10,000 psi. Other well known blendingtechniques may also be used. The amount of metal cation salt utilized toproduce the new metal cation neutralized high acid based ionomer resinsis the quantity which provides a sufficient amount of the metal cationsto neutralize the desired percentage of the carboxylic acid groups inthe high acid copolymer. The extent of neutralization is generally fromabout 10% to about 90%.

As indicated below in Table 5 and more specifically in Example 1 in U.S.application Ser. No. 08/493,089, issued as U.S. Pat. No. 5,688,869, anumber of new types of metal cation neutralized high acid ionomers canbe obtained from the above indicated process. These include new highacid ionomer resins neutralized to various extents with manganese,lithium, potassium, calcium and nickel cations. In addition, when a highacid ethylene/acrylic acid copolymer is utilized as the base copolymercomponent of the invention and this component is subsequentlyneutralized to various extents with the metal cation salts producingacrylic acid based high acid ionomer resins neutralized with cationssuch as sodium, potassium, lithium, zinc, magnesium, manganese, calciumand nickel, several new cation neutralized acrylic acid based high acidionomer resins are produced.

TABLE 5 Shore D Formulation No. Wt-% Cation Salt Wt % NeutralizationMelt Index C.O.R. Hardness  1 (NaOH) 6.98 67.5 0.9 .804 71  2 (NaOH)5.66 54.0 2.4 .808 73  3 (NaOH) 3.84 35.9 12.2 .812 69  4 (NaOH) 2.9127.0 17.5 .812 (brittle)  5 (MnAc) 19.6 71.7 7.5 .809 73  6 (MnAc) 23.188.3 3.5 .814 77  7 (MnAc) 15.3 53.0 7.5 .810 72  8 (MnAc) 26.5 106 0.7.813 (brittle)  9 (LiOH) 4.54 71.3 0.6 .810 74 10 (LiOH) 3.38 52.5 4.2.818 72 11 (LiOH) 2.34 35.9 18.6 .815 72 12 (KOH) 5.30 36.0 19.3 Broke70 13 (KOH) 8.26 57.9 7.18 .804 70 14 (KOH) 10.7 77.0 4.3 .801 67 15(ZnAc) 17.9 71.5 0.2 .806 71 16 (ZnAc) 13.9 53.0 0.9 .797 69 17 (ZnAc)9.91 36.1 3.4 .793 67 18 (HgAc) 17.4 70.7 2.8 .814 74 19 (HgAc) 20.687.1 1.5 .815 76 20 (HgAc) 13.8 53.8 4.1 .814 74 21 (CaAc) 13.2 69.2 1.1.813 74 22 (CaAc) 7.12 34.9 10.1 .808 70 Controls: Hardness 50/50 Blendof Ioteks ® 8000/7030 C.O.R. = 810/65 Shore D Hardness DuPont High AcidSurlyn ® 8422 (Na) C.O.R. = 811/70 Shore D Hardness DuPont High AcidSurlyn ® 8162 (Zn) C.O.R. = 807/65 Shore D Hardness Exxon High AcidIotek ® EX-960 (Zn) C.O.R. = 796/65 Shore D 23 (HgO) 2.91 53.5 2.5 .81324 (HgO) 3.85 71.5 2.8 .808 25 (HgO) 4.76 89.3 1.1 .809 26 (HgO) 1.9635.7 7.5 .815 Control for formulation 23-26 is 50/50 Iotek ® 8000/7030C.O.R. = 814, Formulation 26 C.O.R. was normalized to that controlaccordingly 27 (NiAc) 13.04 61.1 0.2 .802 71 28 (NiAc) 10.71 48.9 0.5.799 72 29 (NiAc) 8.26 36.7 1.8 .796 63 30 (NiAc) 5.66 24.4 7.5 .786 64Control for Formulation No. 27-30 is 50/50 Iotek 8000/7030, C.O.R. =.807When compared to low acid versions of similar cation neutralized ionomerresins, the new metal cation neutralized high acid ionomer resinsexhibit enhanced hardness, modulus and resilience characteristics. Theseare properties that are particularly desirable in a number ofthermoplastic fields, including the field of golf ball manufacturing.

When utilized in the construction of the inner layer of a multi-layeredgolf ball, it has been found that the new acrylic acid based high acidionomers extend the range of hardness beyond that previously obtainablewhile maintaining the beneficial properties (i.e. durability, click,feel, etc.) of the softer low acid ionomer covered balls, such as ballsproduced utilizing the low acid ionomers disclosed in U.S. Pat. Nos.4,884,814 and 4,911,451.

Moreover, as a result of the development of a number of new acrylic acidbased high acid ionomer resins neutralized to various extents by severaldifferent types of metal cations, such as manganese, lithium, potassium,calcium and nickel cations, several new ionomers or ionomer blends arenow available for production of an inner cover layer of a multi-layeredgolf ball. By using these high acid ionomer resins, harder, stifferinner cover layers having higher C.O.R.s, and thus longer distance, canbe obtained.

More preferably, it has been found that when two or more of theabove-indicated high acid ionomers, particularly blends of sodium andzinc high acid ionomers, are processed to produce the covers ofmulti-layered golf balls, (i.e., the inner cover layer herein) theresulting golf balls will travel further than previously knownmulti-layered golf balls produced with low acid ionomer resin covers dueto the balls' enhanced coefficient of restitution values.

The low acid ionomers which may be suitable for use in formulating theinner layer compositions of the second and third embodiments of thesubject invention are ionic copolymers which are the metal, i.e.,sodium, zinc, magnesium, etc., salts of the reaction product of anolefin having from about 2 to 8 carbon atoms and an unsaturatedmonocarboxylic acid having from about 3 to 8 carbon atoms. Preferably,the ionomeric resins are copolymers of ethylene and either acrylic ormethacrylic acid. In some circumstances, an additional comonomer such asan acrylate ester (i.e., iso- or n-butylacrylate, etc.) can also beincluded to produce a softer terpolymer. The carboxylic acid groups ofthe copolymer are partially neutralized (i.e., approximately 10-100%,preferably 30-70%) by the metal ions. Each of the low acid ionomerresins which may be included in the inner layer cover compositions ofthe invention contains 16% by weight or less of a carboxylic acid.

The inner layer compositions include the low acid ionomers such as thosedeveloped and sold by E.I. DuPont de Nemours & Company under thetrademark Surlyn® and by Exxon Corporation under the trademark Escor® ortrademark Iotek®, or blends thereof.

The low acid ionomer resins available from Exxon under the designationEscor® and/or Iotek®, are somewhat similar to the low acid ionomericresins available under the Surlyn® trademark. However, since theEscor®/Iotek® ionomeric resins are sodium or zinc salts ofpoly(ethylene-acrylic acid) and the Surlyn® resins are zinc, sodium,magnesium, etc. salts of poly(ethylene-methacrylic acid), distinctdifferences in properties exist.

When utilized in the construction of the inner layer of a multi-layeredgolf ball, it has been found that the low acid ionomer blends extend therange of compression and spin rates beyond that previously obtainable.More preferably, it has been found that when two or more low acidionomers, particularly blends of sodium and zinc ionomers, are processedto produce the covers of multi-layered golf balls, (i.e., the innercover layer herein) the resulting golf balls will travel further and atan enhanced spin rate than previously known multi-layered golf balls.Such an improvement is particularly noticeable in enlarged or oversizedgolf balls.

As shown in the Examples, use of an inner layer formulated from blendsof lower acid ionomers produces multi-layer golf balls having enhancedcompression and spin rates. These are the properties desired by the moreskilled golfer.

In one embodiment of the inner cover layer, a blend of high and low acidionomer resins is used. These can be the ionomer resins described above,combined in a weight ratio which preferably is within the range of 10-90to 90-10 high and low acid ionomer resins.

Another embodiment of the inner cover layer is primarily or fullynon-ionomeric thermoplastic material. Suitable non-ionomeric materialsinclude metallocene catalyzed polyolefins or polyamides,polyamide/ionomer blends, polyphenylene ether/ionomer blends, etc.,which have a Shore D hardness of at least 60 and a flex modulus ofgreater than about 30,000 psi, or other hardness and flex modulus valueswhich are comparable to the properties of the ionomers described above.Other suitable materials include but are not limited to thermoplastic orthermosetting polyurethanes, thermoplastic block polyesters, e.g., apolyester elastomer such as that marketed by DuPont under the trademarkHytrel®, or thermoplastic block polyamides, e.g., a polyether amide suchas that marketed by Elf Atochem S.A. under the trademark Pebax®, a blendof two or more non-ionomeric thermoplastic elastomers, or a blend of oneor more ionomers and one or more non-ionomeric thermoplastic elastomers.These materials can be blended with the ionomers described above inorder to reduce cost relative to the use of higher quantities ofionomer.

Outer Cover Layer

While the core with the hard inner cover layer formed thereon providesthe multi-layer golf ball with power and distance, the outer cover layer16 is comparatively softer than the inner cover layer. The softnessprovides for the feel and playability characteristics typicallyassociated with balata or balata-blend balls. The outer cover layer orply is comprised of a relatively soft, low modulus (about 1,000 psi toabout 10,000 psi) and, in one embodiment, low acid (less than 16 weightpercent acid) ionomer, an ionomer blend, a non-ionomeric thermoplasticor thermosetting material such as, but not limited to, a metallocenecatalyzed polyolefin such as Exact® material available from Exxon®, athermoplastic or thermoset polyurethane, thermoplastic block polyesters,e.g., a polyester elastomer such as that marketed by DuPont under thetrademark Hytrel®, or thermoplastic block polyamides, such as apolyether amide such as that marketed by Elf Atochem S.A. under thetrademark Pebax®, a blend of two or more non-ionomeric thermoplastic orthermosetting materials, or a blend of one or more ionomers and one ormore non-ionomeric thermoplastic materials. The outer layer is 0.010 toabout 0.15 inches in thickness, preferably 0.01-0.10 inches inthickness, more desirably 0.03 to 0.06 inches in thickness for a 1.680inch ball and 0.04 to 0.07 inches in thickness for a 1.72 inch or moreball), but thick enough to achieve desired playability characteristicswhile minimizing expense. Thickness is defined as the average thicknessof the non-dimpled areas of the outer cover layer. The outer cover layer16 has a Shore D hardness of 55 or less, and more preferably 50 or less.

In one embodiment, the outer cover layer preferably is formed from anionomer which constitutes at least 75 weight % of an acrylateester-containing ionic copolymer or blend of acrylate ester-containingionic copolymers. This type of outer cover layer in combination with thecore and inner cover layer described above results in golf ball covershaving a favorable combination of durability and spin rate. The one ormore acrylate ester-containing ionic copolymers each contain an olefin,an acrylate ester, and an acid. In a blend of two or more acrylateester-containing ionic copolymers, each copolymer may contain the sameor a different olefin, acrylate ester and acid than are contained in theother copolymers. Preferably, the acrylate ester-containing ioniccopolymer or copolymers are terpolymers, but additional monomers can becombined into the copolymers if the monomers do not substantially reducethe scuff resistance or other good playability properties of the cover.

For a given copolymer, the olefin is selected from the group consistingof olefins having 2 to 8 carbon atoms, including, as non-limitingexamples, ethylene, propylene, butene-1, hexene-1 and the like.Preferably the olefin is ethylene.

The acrylate ester is an unsaturated monomer having from 1 to 21 carbonatoms which serves as a softening comonomer. The acrylate esterpreferably is methyl, ethyl, n-propyl, n-butyl, n-octyl, 2-ethylhexyl,or 2-methoxyethyl 1-acrylate, and most preferably is methyl acrylate orn-butyl acrylate. Another suitable type of softening comonomer is analkyl vinyl ether selected from the group consisting of n-butyl,n-hexyl, 2-ethylhexyl, and 2-methoxyethyl vinyl ethers.

The acid is a mono- or dicarboxylic acid and preferably is selected fromthe group consisting of methacrylic, acrylic, ethacrylic,α-chloroacrylic, crotonic, maleic, fumaric, and itaconic acid, or thelike, and half esters of maleic, fumaric and itaconic acid, or the like.The acid group of the copolymer is 10-100% neutralized with any suitablecation, for example, zinc, sodium, magnesium, lithium, potassium,calcium, manganese, nickel, chromium, tin, aluminum, or the like. It hasbeen found that particularly good results are obtained when theneutralization level is about 50-100%.

The one or more acrylate ester-containing ionic copolymers each has anindividual Shore D hardness of about 5-64. The overall Shore D hardnessof the outer cover is 55 or less, and generally is 40-55. It ispreferred that the overall Shore D hardness of the outer cover is in therange of 40-50 in order to impart particularly good playabilitycharacteristics to the ball.

The outer cover layer of the invention is formed over a core to resultin a golf ball having a coefficient of restitution of at least 0.770,more preferably at least 0.780, and most preferably at least 0.790. Thecoefficient of restitution of the ball will depend upon the propertiesof both the core and the cover. The PGA compression of the golf ball is100 or less, and preferably is 90 or less.

The acrylate ester-containing ionic copolymer or copolymers used in theouter cover layer can be obtained by neutralizing commercially availableacrylate ester-containing acid copolymers such as polyethylene-methylacrylate-acrylic acid terpolymers, including Escor® ATX (Exxon ChemicalCompany) or poly (ethylene-butyl acrylate-methacrylic acid) terpolymers,including Nucrel® (DuPont Chemical Company). Particularly preferredcommercially available materials include ATX 320, ATX 325, ATX 310, ATX350, and blends of these materials with Nucrel® 010 and Nucrel® 035. Theacid groups of these materials and blends are neutralized with one ormore of various cation salts including zinc, sodium, magnesium, lithium,potassium, calcium, manganese, nickel, etc. The degree of neutralizationranges from 10-100%. Generally, a higher degree of neutralizationresults in a harder and tougher cover material. The properties ofnon-limiting examples of commercially available un-neutralized acidterpolymers which can be used to form the golf ball outer cover layersof the invention are provided below in Table 6.

TABLE 6 Melt Index Flex modulus dg/min Acid No. MPa Hardness Trade NameASTM D1238 % KOH/g (ASTM D790) (Shore D) ATX 310 6 45 80 44 ATX 320 5 4550 34 ATX 325 20 45 9 30 ATX 350 6 15 20 28 Nucrel ® 010 11 60 40 40Nucrel ® 035 35 60 59 40

The ionomer resins used to form the outer cover layers can be producedby reacting the acrylate ester-containing acid copolymer with variousamounts of the metal cation salts at a temperature above the crystallinemelting point of the copolymer, such as a temperature from about 200° F.to about 500° F., preferably from about 250° F. to about 350° F., underhigh shear conditions at a pressure of from about 100 psi to 10,000 psi.Other well known blending techniques may also be used. The amount ofmetal cation salt utilized to produce the neutralized ionic copolymersis the quantity which provides a sufficient amount of the metal cationsto neutralize the desired percentage of the carboxylic acid groups inthe high acid copolymer. When two or more different copolymers are to beused, the copolymers can be blended before or after neutralization.Generally, it is preferable to blend the copolymers before they areneutralized to provide for optimal mixing.

The compatibility of the acrylate ester-containing copolymers with eachother in a copolymer blend produces a golf ball outer cover layer havinga surprisingly good scuff resistance for a given hardness of the outercover layer. The golf ball according to the invention has a scuffresistance of no higher than 3.0. It is preferred that the golf ball hasa scuff resistance of no higher than about 2.5 to ensure that the golfball is scuff resistant when used in conjunction with a variety of typesof clubs, including sharp-grooved irons, which are particularly inclinedto result in scuffing of golf ball covers. The best results according tothe invention are obtained when the outer cover layer has a scuffresistance of no more than about 2.0. The scuff resistance test isdescribed in detail below.

Additional materials may also be added to the inner and outer coverlayer of the present invention as long as they do not substantiallyreduce the playability properties of the ball. Such materials includedyes (for example, Ultramarine Blue™ sold by Whitaker, Clark, andDaniels of South Plainsfield, N.J.) (see U.S. Pat. No. 4,679,795);pigments such as titanium dioxide, zinc oxide, barium sulfate and zincsulfate; UV absorbers; antioxidants; antistatic agents; and stabilizers.Moreover, the cover compositions of the present invention may alsocontain softening agents such as those disclosed in U.S. Pat. Nos.5,312,857 and 5,306,760, including plasticizers, metal stearates,processing acids, etc., and reinforcing materials such as glass fibersand inorganic fillers, as long as the desired properties produced by thegolf ball covers of the invention are not impaired.

The outer layer in another embodiment of the invention includes a blendof a soft (low acid) ionomer resin with a small amount of a hard (highacid) ionomer resin. A low modulus ionomer suitable for use in the outerlayer blend has a flexural modulus measuring from about 1,000 to about10,000 psi, with a hardness of about 20 to about 40 on the Shore Dscale. A high modulus ionomer herein is one which measures from about15,000 to about 70,000 psi as measured in accordance with ASTM methodD-790. The hardness may be defined as at least 50 on the Shore D scaleas measured in accordance with ASTM method D-2240.

Soft ionomers primarily are used in formulating the hard/soft blends ofthe cover compositions. These ionomers include acrylic acid andmethacrylic acid based soft ionomers. They are generally characterizedas comprising sodium, zinc, or other mono- or divalent metal cationsalts of a terpolymer of an olefin having from about 2 to 8 carbonatoms, methacrylic acid, acrylic acid, or another α, β-unsaturatedcarboxylic acid, and an unsaturated monomer of the acrylate ester classhaving from 1 to 21 carbon atoms. The soft ionomer is preferably madefrom an acrylic acid base polymer in an unsaturated monomer of theacrylate ester class.

Certain ethylene-acrylic acid based soft ionomer resins developed by theExxon Corporation under the designation Iotek® 7520 (referred toexperimentally by differences in neutralization and melt indexes as LDX195, LDX 196, LDX 218 and LDX 219) may be combined with known hardionomers such as those indicated above to produce the inner and outercover layers. The combination produces higher C.O.R.s at equal or softerhardness, higher melt flow (which corresponds to improved, moreefficient molding, i.e., fewer rejects) as well as significant costsavings versus the outer layer of multi-layer balls produced by otherknown hard-soft ionomer blends as a result of the lower overall rawmaterials costs and improved yields.

Test data collected indicates that Iotek® 7520 resins have Shore Dhardnesses of about 32 to 36 (per ASTM D-2240), melt flow indexes of3±0.5 g/10 min (at 190° C. per ASTM D-1288), and a flexural modulus ofabout 2500-3500 psi (per ASTM D-790). Furthermore, testing by anindependent testing laboratory by pyrolysis mass spectrometry indicatesthat Iotek® 7520 resins are generally zinc salts of a terpolymer ofethylene, acrylic acid, and methyl acrylate.

Furthermore, it has been found that a grade of an acrylic acid basedsoft ionomer available from the Exxon Corporation under the designationIotek® 7510 is also effective when combined with the hard ionomersindicated above in producing golf ball covers exhibiting higher C.O.R.values at equal or softer hardness than those produced by knownhard-soft ionomer blends. In this regard, Iotek® 7510 has the advantages(i.e. improved flow, higher C.O.R. values at equal hardness, increasedclarity, etc.) produced by the Iotek®7520 resin when compared to themethacrylic acid base soft ionomers known in the art (such as theSurlyn® 8625 and the Surlyn® 8629 combinations disclosed in U.S. Pat.No. 4,884,814).

In addition, Iotek® 7510, when compared to Iotek® 7520, producesslightly higher C.O.R. values at equal softness/hardness due to theIotek® 7510's higher hardness and neutralization. Similarly, Iotek® 7510produces better release properties (from the mold cavities) due to itsslightly higher stiffness and lower flow rate than Iotek® 7520. This isimportant in production where the soft covered balls tend to have loweryields caused by sticking in the molds and subsequent punched pin marksfrom the knockouts.

According to Exxon, Iotek® 7510 is of similar chemical composition asIotek® 7520 (i.e. a zinc salt of a terpolymer of ethylene, acrylic acid,and methyl acrylate) but is more highly neutralized. Based upon FTIRanalysis, Iotek® 7520 is estimated to be about 30-40 wt.-% neutralizedand Iotek® 7610 is estimated to be about 40-60 wt.-% neutralized. Thetypical properties of Iotek® 7510 in comparison of those of Iotek® 7520in comparison of those of Iotek® 7520 are set forth below:

TABLE 7 Physical Properties of Iotek ® 7510 in Comparison to Iotek ®7520 Property Unit Iotek ® 7520 Iotek ® 7510 Melt Index g/10 min. 2.00.8 Density g/cc 0.96 0.97 Melting Point ° F. 151 149 Vicat Softening °F. 108 109 Point Flex Modulus psi 3800 5300 Tensile Strength psi 14501750 Elongation % 760 690 Hardness, Shore D — 32 35

The hard ionomer resins utilized to produce the outer cover layercomposition hard/soft blends include ionic copolymers which are thesodium, zinc, magnesium, lithium, etc. salts of the reaction product ofan olefin having from 2 to 8 carbon atoms and an unsaturatedmonocarboxylic acid having from 3 to 8 carbon atoms. The carboxylic acidgroups of the copolymer may be totally or partially (i.e. approximately15-75 percent) neutralized.

The hard ionomeric resins are likely copolymers of ethylene and acrylicand/or methacrylic acid, with copolymers of ethylene and acrylic acidbeing the most preferred. Two or more types of hard ionomeric resins maybe blended into the outer cover layer compositions in order to producethe desired properties of the resulting golf balls.

As discussed earlier herein, the hard ionomeric resins introduced underthe designation Escor® and sold under the designation Iotek® aresomewhat similar to the hard ionomeric resins sold under the Surlyn®trademark. However, since the Iotek® ionomeric resins are sodium or zincsalts of poly(ethylene-acrylic acid) and the Surlyn® resins are zinc orsodium salts of poly(ethylene-methacrylic acid) some distinctdifferences in properties exist. As more specifically indicated in thedata set forth below, the hard Iotek® resins (i.e., the acrylic acidbased hard ionomer resins) are the more preferred hard resins for use informulating the layer blends for use in the present invention. Inaddition, various blends of Iotek® and Surlyn® hard ionomeric resins, aswell as other available ionomeric resins, may be utilized in the presentinvention in a similar manner.

Examples of commercially available hard ionomeric resins which may beused in the present invention in formulating the outer cover blendsinclude the hard sodium ionic copolymer sold under the trademark Surlyn®8940 and the hard zinc ionic copolymer sold under the trademark Surlyn®9910. Surlyn® 8940 is a copolymer of ethylene with methacrylic acid andabout 15 weight percent acid which is about 29 percent neutralized withsodium ions. This resin has an average melt flow index of about 2.8.Surlyn® 9910 is a copolymer of ethylene and methacrylic acid with about15 weight percent acid which is about 58 percent neutralized with zincions. The average melt flow index of Surlyn® 9910 is about 0.7. Thetypical properties of Surlyn® 9910 and 8940, as well as other Surlyn®resins, are set forth below in Tables 8 and 9:

TABLE 8 Typical Properties of Commercially Available Hard Surlyn ®Resins Suitable for Use in the Present Invention ASTM D 8940 9910 89208528 9970 9730 Cation type Sodium Zinc Sodium Sodium Zinc Zinc Melt flowindex, gms/10 min. D-1238    2.8    0.7    0.9    1.3    14.0    1.6Specific gravity, g/cm³ D-792    0.95    0.97    0.95    0.94    0.95   0.95 Hardness, Shore D D-2240  65  64  66  60  62  63 Tensilestrength, (kpsi) D-638    (4.8)    (3.6)    (5.4)    (4.2)    (3.2)   (4.1) MPa   33.1   24.8   37.2   29.0   22.1   28.3 Elongation, %D-638 470 290 350 450 460 460 Flexural Modulus, (kpsi) D-790  (51)  (48) (55)  (32)  (28)  (30) MPa 350 330 380 220 190 210 Tensile Impact (23°C.), D-1822S 1020  1020  865 1160  760 1240  KJ/m² (ft.-lbs./in²) (485)(485) (410) (550) (360) (590) Vicat Temperature, ° C. D-1525  63  62  58 73  61  73

TABLE 9 Properties of Additional Hard Surlyn ® Resins SURLYN ® SURLYN ®SURLYN ® Ionomer 8920 8140 9120 Cation Na Na Na Melt Flow Index gms/ 0.92.6 1.3 10 min. MP ° C. 84 88 85 FP ° C. 52 49 50 Tensile Strength kpsi5.4 5.0 3.8 Yield Strength kpsi 2.2 2.8 2.4 Elongation % 350 340 280Flex Modulus kpsi 55 71 64 Shore D Hardness 66 70 69

Examples of the more pertinent acrylic acid based hard ionomer resinsuitable for use in the cover compositions sold under the Iotek®tradename by the Exxon Corporation include Iotek®, but are not limitedto, 8000, 8010, 8020, 8030, 7030, 7010, 7020, EX 1001-1009, Iotek® 959and Iotek® 960, as well as the materials listed above on Tables 2 and 3.The typical properties of the remainder of these and other Iotek®ionomers suited for use in formulating the cover compositions are setforth below in Tables 10 and 11:

TABLE 10 Typical Properties of Iotek ® Ionomers ASTM Resin PropertiesMethod Units 7010 7020 7030 8000 8020 8030 Cation type zinc zinc zincsodium sodium sodium Melt Index D-1238 g/10 min 0.8 1.5 2.5 0.8 1.6 2.8Density D-1505 kg/m3 968 966 964 957 956 956 Melting Point D-3417 ° C.83.5 84 85 83 84 87 Crystallization D-3417 ° C. 55 56 58 45 47 49 PointVicat Softening D-1525 ° C. 60 60 60 54 54.5 55.5 Point Tensile strengthD-638 MPa 24.5 23.5 22.6 33 32.5 32 at break Yield Strength D-638 MPa 1413 12 19 18.5 18 Elongation at D-638 % 440 450 460 370 380 410 break 1%Secant D-638 MPa 150 135 125 280 280 280 Modulus Shore Hardness, DD-2240 — 54 53 52 60 60 60 Flex Modulus D-790 MPa 190 175 155 320 340355 (3 mm)

TABLE 11 Additional Examples of Exxon Ionomers PROPERTY Ex 1005 Ex 1006Ex 1007 Ex 1008 Ex 1009 7310 Melt Index, 0.7 1.3 1.0 1.4 0.8 1.0 g/10min. Cation Na Na Zn Zn Na Zn Melting Point, 85.3 86 85.8 86 91.3 91 °C. Vicat Softening 54 57 60.5 60 56 69 Point, ° C. Tensile @ break, 33.933.5 24.1 23.6 32.4 24 MPa Elongation @ 403 421 472 427 473 520 Break, %Hardness, 58 58 51 50 56 52 Shore D Flexural 289 290 152 141 282 150Modulus, MPa

It has been determined that when hard/soft ionomer blends are used forthe outer cover layer, good results are achieved when the relativecombination is in a range of about 3-25 percent hard ionomer and about75-97 percent soft ionomer.

Moreover, in alternative embodiments, either the inner and/or the outercover layer may also comprise up to 100 wt % of a soft, low modulus,non-ionomeric thermoplastic or thermoset material. Non-ionomericmaterials are suitable so long as they produce the playability anddurability characteristics desired without adversely affecting theenhanced travel distance characteristic produced by the high acidionomer resin composition. These include but are not limitedstyrene-butadiene-styrene block copolymers, including functionalizedstyrene-butadiene-styrene block copolymers,styrene-ethylene-butadiene-styrene (SEBS) block copolymers such asKraton® materials from Shell Chem. Co., and functionalized SEBS blockcopolymers; metallocene catalyzed polyolefins; ionomer/rubber blendssuch as those in Spalding U.S. Pat. Nos. 4,986,545; 5,098,105 and5,187,013; and, Hytrel® polyester elastomers from DuPont and Pebax®polyetheramides from Elf Atochem S.A.

A preferred non-ionomeric material suitable for the inner and/or outercover layer includes polyurethane. Polyurethanes are polymers which areused to form a broad range of products. They are generally formed bymixing two primary ingredients during processing. For the most commonlyused polyurethanes, the two primary ingredients are a polyisocyanate(for example, diphenylmethane diisocyanate monomer (“MDI”) and toluenediisocyanate (“TDI”) and their derivatives) and a polyol (for example, apolyester polyol or a polyether polyol).

A wide range of combinations of polyisocyanates and polyols, as well asother ingredients, are available. Furthermore, the end-use properties ofpolyurethanes can be controlled by the type of polyurethane utilized,i.e., whether the material is thermoset (cross linked molecularstructure) or thermoplastic (linear molecular structure).

Cross linking occurs between the isocyanate groups (—NCO) and thepolyol's hydroxyl end-groups (—OH). Additionally, the end-usecharacteristics of polyurethanes can also be controlled by differenttypes of reactive chemicals and processing parameters. For example,catalysts are utilized to control polymerization rates. Depending uponthe processing method, reaction rates can be very quick (as in the casefor some reaction injection molding systems (i.e., “RIM”) or may be onthe order of several hours or longer (as in several coating systems).Consequently, a great variety of polyurethanes are suitable fordifferent end-uses.

Polyurethanes are typically classified as thermosetting orthermoplastic. A polyurethane becomes irreversibly “set” when apolyurethane prepolymer is cross linked with a polyfunctional curingagent, such as a polyamine or a polyol. The prepolymer typically is madefrom polyether or polyester. Diisocyanate polyethers are preferredbecause of their water resistance.

The physical properties of thermoset polyurethanes are controlledsubstantially by the degree of cross linking. Tightly cross linkedpolyurethanes are fairly rigid and strong. A lower amount of crosslinking results in materials that are flexible and resilient.Thermoplastic polyurethanes have some cross linking, but primarily byphysical means. The crosslinkings bonds can be reversibly broken byincreasing temperature, as occurs during molding or extrusion. In thisregard, thermoplastic polyurethanes can be injection molded, andextruded as sheet and blow film. They can be used up to about 350° F.and are available in a wide range of hardnesses.

Polyurethane materials suitable for the present invention are formed bythe reaction of a polyisocyanate, a polyol, and optionally one or morechain extenders. The polyol component includes any suitable polyether-or polyesterpolyol. Additionally, in an alternative embodiment, thepolyol component is polybutadiene diol. The chain extenders include, butare not limited, to diols, triols and amine extenders. Any suitablepolyisocyanate may be used to form a polyurethane according to thepresent invention. The polyisocyanate is preferably selected from thegroup of diisocyanates including, but not limited, to4,4′-diphenylmethane diisocyanate (“MDI”); 2,4-toluene diisocyanate(“TDI”); m-xylylene diisocyanate (“XDI”); methylene bis-(4-cyclohexylisocyanate) (“HMDI”); hexamethylene diisocyanate (HDI);naphthalene-1,5,-diisocyanate (“NDI”); 3,3′-dimethyl-4,4′-biphenyldiisocyanate (“TODI”); 1,4-diisocyanate benzene (“PPDI”);phenylene-1,4-diisocyanate; and 2,2,4- or 2,4,4-trimethyl hexamethylenediisocyanate (“TMDI”).

Other less preferred diisocyanates include, but are not limited to,isophorone diisocyanate (“IPDI”); 1,4-cyclohexyl diisocyanate (“CHDI”);diphenylether-4,4′-diisocyanate; p,p′-diphenyl diisocyanate; lysinediisocyanate (“LDI”); 1,3-bis (isocyanato methyl)cyclohexane; andpolymethylene polyphenyl isocyanate (“PMDI”).

One polyurethane component which can be used in the present inventionincorporates TMXDI (“META”) aliphatic isocyanate (Cytec Industries, WestPaterson, N.J.). Polyurethanes based on meta-tetramethylxylylenediisocyanate (TMXDI) can provide improved gloss retention UV lightstability, thermal stability, and hydrolytic stability. Additionally,TMXDI (“META”) aliphatic isocyanate has demonstrated favorabletoxicological properties. Furthermore, because it has a low viscosity,it is usable with a wider range of diols (to polyurethane) and diamines(to polyureas). If TMXDI is used, it typically, but not necessarily, isadded as a direct replacement for some or all of the other aliphaticisocyanates in accordance with the suggestions of the supplier. Becauseof slow reactivity of TMXDI, it may be useful or necessary to usecatalysts to have practical demolding times. Hardness, tensile strengthand elongation can be adjusted by adding further materials in accordancewith the supplier's instructions.

The polyurethane which is selected for use as a golf ball coverpreferably has a Shore D hardness of from about 10 to about 55, morepreferably from about 30 to about 55, and most preferably from about 30to about 53 for a soft cover layer. The polyurethane which is to be usedfor a cover layer preferably has a flex modulus from about 1 to about310 Kpsi, more preferably from about 5 to about 100 Kpsi, and mostpreferably from about 5 to about 20 Kpsi for a soft cover layer and 30to 70 Kpsi for a hard cover layer. Accordingly, covers comprising thesematerials exhibit similar properties.

A non-limiting example of a polyurethane suitable for use in the outercover layer includes a polyester polyurethane such as B.F. GoodrichCompany's Estane® polyester polyurethane X-4517. The non-ionomericthermoplastic material may be blended with a soft ionomer. For example,polyamides blend well with soft ionomer. According to B.F. Goodrich,Estane® X-4517 has the following properties:

TABLE 12 Properties of Estane ® X-4517 Tensile 1430 100% 815 200% 1024300% 1193 Elongation 641 Youngs Modulus 1826 Hardness A/D 88/39 BayshoreRebound 59 Solubility in Water Insoluble Melt processingtemperature >350° F. (>177° C.) Specific Gravity (H₂O = 1) 1.1-1.3

Other soft, relatively low modulus non-ionomeric thermoplastic orthermoset polyurethanes may also be utilized to produce the inner and/orouter cover layers as long as the non-ionomeric materials produce theplayability and durability characteristics desired without adverselyaffecting the enhanced travel distance characteristic produced by thehigh acid ionomer resin composition. These include, but are not limitedto thermoplastic polyurethanes such as Texin® thermoplasticpolyurethanes from Mobay Chemical Co. and the Pellethane® thermoplasticpolyurethanes from Dow Chemical Co.; and non-ionomeric thermosetpolyurethanes including but not limited to those disclosed in U.S. Pat.No. 5,334,673.

Other suitable polyurethane materials for use in the present inventiongolf balls include reaction injection molded (“RIM”) polyurethanes RIMis a process by which highly reactive liquids are injected into a closedmold, mixed usually by impingement and/or mechanical mixing in anin-line device such as a “peanut mixer,” where they polymerize primarilyin the mold to form a coherent, one-piece molded article. The RIMprocess usually involves a rapid reaction between one or more reactivecomponents such as polyether—or polyester—polyol, polyamine, or othermaterial with an active hydrogen, and one or more isocyanate—containingconstituents, often in the presence of a catalyst. The constituents arestored in separate tanks prior to molding and may be first mixed in amix head upstream of a mold and then injected into the mold. The liquidstreams are metered in the desired weight to weight ratio and fed intoan impingement mix head, with mixing occurring under high pressure,e.g., 1,500 to 3,000 psi. The liquid streams impinge upon each other inthe mixing chamber of the mix head and the mixture is injected into themold. One of the liquid streams typically contains a catalyst for thereaction. The constituents react rapidly after mixing to gel and formpolyurethane polymers. Polyureas, epoxies, and various unsaturatedpolyesters also can be molded by RIM.

Non-limiting examples of suitable RIM systems for use in the presentinvention are Bayflex® elastomeric polyurethane RIM systems, Baydur® GSsolid polyurethane RIM systems, Prism® solid polyurethane RIM systems,all from Bayer Corp. (Pittsburgh, Pa.), Spectrim® reaction moldablepolyurethane and polyurea systems from Dow Chemical USA (Midland,Mich.), including Spectrim® MM 373-A (isocyanate) and 373-B (polyol),and Elastolit® SR systems from BASF (Parsippany, N.J.). Preferred RIMsystems include Bayflex® MP-10000 and Bayflex® 110-50, filled andunfilled. Further preferred examples are polyols, polyamines andisocyanates formed by processes for recycling polyurethanes andpolyureas. Additionally, these various systems may be modified byincorporating a butadiene component in the diol agent.

A preferred form of the invention is a golf ball in which at least oneof the inner cover layer and/or the outer cover layer comprises afast-chemical-reaction-produced component. This component comprises atleast one material selected from the group consisting of polyurethane,polyurea, polyurethane ionomer, epoxy, and unsaturated polyesters, andpreferably comprises polyurethane. A particularly preferred form of theinvention is a golf ball with a cover comprising polyurethane.

The method of the invention is particularly useful in forming golf ballsbecause it can be practiced at relatively low temperatures andpressures. The preferred temperature range for the method of theinvention is from about 90 to about 180° F. when the component beingproduced contains polyurethane. Preferred pressures for practicing theinvention using polyurethane-containing materials are 200 psi or lessand more preferably 100 psi or less. The method of the present inventionoffers numerous advantages over conventional slow-reactive processcompression molding of golf ball covers. The method of the presentinvention results in molded covers in a demold time of 10 minutes orless, preferably 2 minutes or less, and most preferably in 1 minute orless. The method of the present invention results in the formation of areaction product formed by mixing two or more reactants together, thatexhibits a reaction time of about 2 minutes or less, preferably oneminute or less, and most preferably about 30 seconds or less. The termfast-chemical-reaction-produced component as used herein refers to suchreaction products. An excellent finish can be produced on the ballutilizing these components and molding techniques.

The polyol component typically contains additives, such as stabilizers,flow modifiers, catalysts, combustion modifiers, blowing agents,fillers, pigments, optical brighteners, and release agents to modifyphysical characteristics of the cover. Polyurethane/polyurea constituentmolecules that were derived from recycled polyurethane can be added inthe polyol component.

A golf ball inner cover layer according to the present invention formedfrom a polyurethane material typically contains from about 0 to about 60weight percent of filler material, more preferably from about 1 to about30 weight percent, and most preferably from about 1 to about 20 weightpercent.

A golf ball outer cover layer according to the present invention formedfrom a polyurethane material typically contains from about 0 to about 20weight percent of filler material, more preferably from about 1 to about10 weight percent, and most preferably from about 1 to about 5 weightpercent.

Core

The cores of the inventive golf balls typically have a coefficient ofrestitution of about 0.750 or more, more preferably 0.770 or more and aPGA compression of about 90 or less, and more preferably 70 or less.Furthermore, in some applications it may be desirable to provide a corewith a coefficient of restitution of about 0.780 to 0.790 or more. Thecore used in the golf ball of the invention preferably is a solid. Theterm “solid cores” as used herein refers not only to one piece cores butalso to those cores having a separate solid layer beneath the covers andover the central core. The cores have a weight of 25-40 grams andpreferably 30-40 grams. When the golf ball of the invention has a solidcore, this core can be compression molded from a slug of uncured orlightly cured elastomer composition comprising a high cis contentpolybutadiene and a metal salt of an α, β, ethylenically unsaturatedcarboxylic acid such as zinc mono- or diacrylate or methacrylate. Toachieve higher coefficients of restitution and/or to increase hardnessin the core, the manufacturer may include a small amount of a metaloxide such as zinc oxide. In addition, larger amounts of metal oxidethan are needed to achieve the desired coefficient may be included inorder to increase the core weight so that the finished ball more closelyapproaches the U.S.G.A. upper weight limit of 1.620 ounces. Non-limitingexamples of other materials which may be used in the core compositionincluding compatible rubbers or ionomers, and low molecular weight fattyacids such as stearic acid. Free radical initiator catalysts such asperoxides are admixed with the core composition so that on theapplication of heat and pressure, a curing or cross-linking reactiontakes place.

A thread wound core may comprise a liquid, solid, gel or multi-piececenter. The thread wound core is typically obtained by winding a threadof natural or synthetic rubber, or thermoplastic or thermosettingelastomer such as polyurethane, polyester, polyamide, etc. on a solid,liquid, gel or gas filled center to form a thread rubber layer that isthen covered with one or more mantle or cover layers. Additionally,prior to applying the cover layers, the thread wound core may be furthertreated or coated with an adhesive layer, protective layer, or anysubstance that may improve the integrity of the wound core duringapplication of the cover layers and ultimately in usage as a golf ball.Since the core material is not an integral part of the presentinvention, further detailed discussion concerning the specific types ofcore materials which may be utilized with the cover compositions of theinvention are not specifically set forth herein.

Since the core material is not an integral part of the presentinvention, a detailed discussion concerning the specific types of corematerials which may be utilized with the cover compositions of theinvention are not specifically set forth herein.

Method of Making Golf Ball

In preparing golf balls in accordance with the present invention, a hardinner cover layer is molded (for example, by injection molding or bycompression molding) about a core (preferably a solid core). Acomparatively softer outer layer is molded over the inner layer.

The solid core for the multi-layer ball is about 1.2-1.6 inches indiameter, although it may be possible to use cores in the range of about1.0-2.0 inches. Conventional solid cores are typically compression orinjection molded from a slug or ribbon of uncured or lightly curedelastomer composition comprising a high cis content polybutadiene and ametal salt of an α, β, ethylenically unsaturated carboxylic acid such aszinc mono or diacrylate or methacrylate. To achieve higher coefficientsof restitution in the core, the manufacturer may include fillers such assmall amounts of a metal oxide such as zinc oxide. In addition, largeramounts of metal oxide than those that are needed to achieve the desiredcoefficient are often included in conventional cores in order toincrease the core weight so that the finished ball more closelyapproaches the U.S.G.A. upper weight limit of 1.620 ounces. Othermaterials may be used in the core composition including compatiblerubbers or ionomers, and low molecular weight fatty acids such asstearic acid. Free radical initiators such as peroxides are admixed withthe core composition so that on the application of heat and pressure, acomplex curing cross-linking reaction takes place.

The inner cover layer which is molded over the core is about 0.01 inchesto about 0.10 inches in thickness, preferably about 0.03-0.07 inchesthick. The inner ball which includes the core and inner cover layerpreferably has a diameter in the range of 1.25 to 1.60 inches. The outercover layer is about 0.01 inches to about 0.10 inches in thickness.Together, the core, the inner cover layer and the outer cover layercombine to form a ball having a diameter of 1.680 inches or more, theminimum diameter permitted by the rules of the United States GolfAssociation and weighing no more than 1.62 ounces.

In a particularly preferred embodiment of the invention, the golf ballhas a dimple pattern which provides coverage of 65% or more. The golfball typically is coated with a durable, abrasion-resistant, relativelynon-yellowing finish coat if necessary.

The various cover composition layers of the present invention may beproduced according to conventional melt blending procedures. Generally,the copolymer resins are blended in a Banbury® type mixer, two-rollmill, or extruder prior to neutralization. After blending,neutralization then occurs in the melt or molten state in the Banbury®mixer. Mixing problems are minimal because preferably more than 75 wt %,and more preferably at least 80 wt % of the ionic copolymers in themixture contain acrylate esters, and in this respect, most of thepolymer chains in the mixture are similar to each other. The blendedcomposition is then formed into slabs, pellets, etc., and maintained insuch a state until molding is desired. Alternatively, a simple dry blendof the pelletized or granulated resins which have previously beenneutralized to a desired extent and colored master batch may be preparedand fed directly into the injection molding machine where homogenizationoccurs in the mixing section of the barrel prior to injection into themold. If necessary, further additives such as an inorganic filler, etc.,may be added and uniformly mixed before initiation of the moldingprocess. A similar process is utilized to formulate the high acidionomer resin compositions used to produce the inner cover layer. In oneembodiment of the invention, a master batch of non-acrylateester-containing ionomer with pigments and other additives incorporatedtherein is mixed with the acrylate ester-containing copolymers in aratio of about 1-7 weight % master batch and 93-99 weight % acrylateester-containing copolymer.

The golf balls of the present invention can be produced by moldingprocesses which include but are not limited to those which are currentlywell known in the golf ball art. For example, the golf balls can beproduced by injection molding or compression molding the novel covercompositions around a wound or solid molded core to produce an innerball which typically has a diameter of about 1.50 to 1.67 inches. Theouter layer is subsequently molded over the inner layer to produce agolf ball having a diameter of 1.620 inches or more, preferably about1.680 inches or more. Although either solid cores or wound cores can beused in the present invention, as a result of their lower cost andsuperior performance, solid molded cores are preferred over wound cores.The standards for both the minimum diameter and maximum weight of theballs are established by the United States Golf Association (U.S.G.A.).

In compression molding, the inner cover composition is formed viainjection at about 380° F. to about 450° F. into smooth surfacedhemispherical shells which are then positioned around the core in a moldhaving the desired inner cover thickness and subjected to compressionmolding at 200° to 300° F. for about 2 to 10 minutes, followed bycooling at 50° to 70° F. for about 2 to 7 minutes to fuse the shellstogether to form a unitary intermediate ball. In addition, theintermediate balls may be produced by injection molding wherein theinner cover layer is injected directly around the core placed at thecenter of an intermediate ball mold for a period of time in a moldtemperature of from 50° to about 100° F. Subsequently, the outer coverlayer is molded about the core and the inner layer by similarcompression or injection molding techniques to form a dimpled golf ballof a diameter of 1.680 inches or more.

After molding, the golf balls produced may undergo various furtherprocessing steps such as buffing, painting and marking as disclosed inU.S. Pat. No. 4,911,451.

The resulting golf ball produced from the hard inner layer and therelatively softer, low flexural modulus outer layer provide for animproved multi-layer golf ball which provides for desirable coefficientof restitution and durability properties while at the same time offeringthe feel and spin characteristics associated with soft balata andbalata-like covers of the prior art.

Additionally, golf balls of the present invention that comprisepolyurethane in any of the inner and outer cover layer may be producedby a reaction injection molding process (RIM). RIM is a process by whichhighly reactive liquids are injected into a closed mold, mixed usuallyby impingement and/or mechanical mixing in an in-line device such as a“peanut mixer,” where they polymerize primarily in the mold to form acoherent, one-piece molded article. The RIM process usually involves arapid reaction between one or more reactive components such aspolyether—or polyester—polyol, polyamine, or other material with anactive hydrogen, and one or more isocyanate—containing constituents,often in the presence of a catalyst. The constituents are stored inseparate tanks prior to molding and may be first mixed in a mix headupstream of a mold and then injected into the mold. The reaction mixtureviscosity should be sufficiently low to ensure that the empty space inthe mold is completely filled. The reactant materials generally arepreheated to 90° F. to 150° F. before they are mixed. In most cases itis necessary to preheat the mold to, e.g., 100 to 180° F., to ensureproper injection viscosity. The liquid streams are metered in thedesired weight to weight ratio and fed into an impingement mix head,with mixing occurring under high pressure, e.g., 1,500 to 3,000 psi. Theliquid streams impinge upon each other in the mixing chamber of the mixhead and the mixture is injected into the mold. Injector nozzles impingethe isocyanate and polyol at ultra-high velocity to provide excellentmixing. Additional mixing may be conducted using an aftermixer, whichtypically is constructed inside the mold between the mix head and themold cavity. One of the liquid streams typically contains a catalyst forthe reaction. The constituents react rapidly after mixing to gel andform polyurethane polymers. Polyureas, epoxies, and various unsaturatedpolyesters also can be molded by RIM.

Golf balls and, more specifically, cover layers formed by RIM arepreferably formed by the process described in application Ser. No.09/040,798, filed Mar. 18, 1998, incorporated herein by reference.

RIM differs from non-reaction injection molding in a number of ways. Themain distinction is that in RIM a chemical reaction takes place in themold to transform a monomer or adducts to polymers and the componentsare in liquid form. Thus, a RIM mold need not be made to withstand thepressures which occur in a conventional injection molding. In contrast,injection molding is conducted at high molding pressures in the moldcavity by melting a solid resin and conveying it into a mold, with themolten resin often being at about 150 to about 350° C. At this elevatedtemperature, the viscosity of the molten resin usually is in the rangeof about 50,000 to about 1,000,000 centipoise, and is typically around200,000 centipoise. In an injection molding process, the solidificationof the resins occurs after about 10 to about 90 seconds, depending uponthe size of the molded product, the temperature and heat transferconditions, and the hardness of the injection molded material.Subsequently, the molded product is removed from the mold. There is nosignificant chemical reaction taking place in an injection moldingprocess when the thermoplastic resin is introduced into the mold. Incontrast, in a RIM process, the chemical reaction causes the material toset in less than about 5 minutes, often in less than 2 minutes,preferably in less than one minute, more preferably in less than 30seconds, and in many cases in about 10 seconds or less.

Catalysts can be added to the RIM polyurethane system starting materialsas long as the catalysts generally do not react with the constituentwith which they are combined. Suitable catalysts include those which areknown to be useful with polyurethanes and polyureas.

The polyol component typically contains additives, such as stabilizers,flow modifiers, catalysts, combustion modifiers, blowing agents,fillers, pigments, optical brighteners, and release agents to modifyphysical characteristics of the cover. Recycled polyurethane/polyureaalso can be added to the core. Polyurethane/polyurea constituentmolecules that were derived from recycled polyurethane can be added inthe polyol component.

The mold cavity contains retractable pins and is generally constructedin the same manner as a mold cavity used to injection mold athermoplastic, e.g., ionomeric golf ball cover. However, two differenceswhen RIM is used are that tighter pin tolerances generally are required,and a lower injection pressure is used. Also, the molds can be producedfrom lower strength material such as aluminum.

RIM may provide for improved cover layers. If plastic products areproduced by combining components that are preformed to some extent,subsequent failure can occur at a location on the cover which is alongthe seam or parting line of the mold. Failure can occur at this locationbecause this interfacial region is intrinsically different from theremainder of the cover layer and can be weaker or more stressed. Coverlayers produced via RIM are believed to provide for improved durabilityof a golf ball cover layer by providing a uniform or “seamless” cover inwhich the properties of the cover material in the region along theparting line are generally the same as the properties of the covermaterial at other locations on the cover, including at the poles. Theimprovement in durability is believed to be a result of the fact thatthe reaction mixture is distributed uniformly into a closed mold. Thisuniform distribution of the injected materials eliminates knit-lines andother molding deficiencies which can be caused by temperature differenceand/or reaction difference in the injected materials. RIM typicallyresults in generally uniform molecular structure, density and stressdistribution as compared to conventional injection-molding processes.

The golf balls formed according to the present invention can be coatedusing a conventional two-component spray coating or can be coated duringthe RIM process, i.e., using an in-mold coating process.

Unique Spin Characteristics

As indicated above, the golf balls of the invention are unique in thatthey provide good distance when hit with a driver, good control off ofirons, and excellent spin on short chip shots. This type of golf ball issuperior to conventional soft covered two-piece or wound balls in thatit has lower spin off of a driver and higher spin on short shots.

The spin factor of the ball of the invention may be specified in themanner described below.

Step 1. A golf ball testing machine is set up in order that it meets thefollowing conditions for hitting a 1995 Top-Flite® Tour Z-balata 90 ballavailable from Spalding Sports Worldwide, Inc.

Club Launch Angle Ball Speed Spin Rate 9 iron 21 ± 1.5 160.5 ± 9.0 9925± 600The machine is set up such that the above conditions are met for eachtest using 10 Z-balata 90 golf balls which are hit 3 times each at thesame machine setting. The thirty measurements of spin rate are averagedto obtain N_(9I-ZB).

Step 2. Ten golf balls of the invention (Ball X) are hit 3 times eachusing the same machine setting as was used for the Z-balata balls andspin data is collected. Any clearly erratic spin test result iseliminated and replaced by a new test with the same ball. The thirtymeasurements of spin rate are averaged to obtain N_(9I-X).

Step 3. The machine is set up in order that it meets the followingconditions for hitting a 1995 Z-balata 90 ball, the conditions beingintended to replicate a 30-yard chip shot:

Club Launch Angle Ball Speed Spin Rate Sand Wedge 28 ± 4.5 58.0 ± 4.04930 ± 770The machine is set up such that the above conditions are met for eachtest using 10 Z-balata 90 golf balls which are hit 3 times each at thesame machine setting. The thirty measurements of spin rate are averagedto obtain N_(SW-ZB).

Step 4. The 10 golf balls used in Step 2 are hit three times each usingthe same machine setting as was used in Step 3 and spin data iscollected. Any clearly erratic spin test result is eliminated andreplaced by a new test with the same ball. The thirty measurements ofspin rate are averaged to obtain N_(SW-X).

Step 5. The numerical values of N_(9I-ZB), N_(9I-X), N_(SW-ZB) andN_(SW-X) are inserted into the following formula to obtain a spinfactor:

${{Spin}\mspace{14mu}{factor}} = {\frac{N_{{SW} - X}}{N_{91 - X}} - {\frac{N_{{SW} - {ZB}}}{N_{91 - {ZB}}} \times 100}}$The golf ball of the invention has a spin factor of 3.0 or more, morepreferably 5.0 or more, and most preferably 8.0 or more.

The present invention is further illustrated by the following examplesin which the parts of the specific ingredients are by weight. It is tobe understood that the present invention is not limited to the examples,and various changes and modifications may be made in the inventionwithout departing from the spirit and scope thereof.

Example 1 Ionic Terpolymer-Containing Cover

A set of two-piece golf balls was made with solid cores and a covercomposition of 75 weight % Nucrel® 035, which is an acrylateester-containing acid terpolymer, and 25 weight % of a master batchcontaining 4.5 weight % MgO in Surlyn® 1605 (“MgO Master batch”). Theterpolymer was reacted with the master batch at a temperature of about250° F. under high shear conditions at a pressure of about 0 to 100 psi.The magnesium in the master batch neutralized acid groups of theterpolymer at a level of about 62% neutralization. The molded balls werefinished with polyurethane primer and top coats. The PGA compression,coefficient of restitution, Shore C hardness, scuff resistance, spinrate and cold crack of the golf balls were determined. The results areshown on Table 13 below.

To measure cold crack, the finished golf balls were stored at −10° F.for at least 24 hours and were then subjected to 5 blows in acoefficient machine at 165 ft/sec. The balls were allowed to return toroom temperature and were then visually inspected for cover cracking.None of the golf balls experienced cracking.

Coefficient of restitution (C.O.R.) was measured by firing the resultinggolf ball in an air cannon at a velocity of 125 feet per second againsta steel plate which was positioned 12 feet from the muzzle of thecannon. The rebound velocity was then measured. The rebound velocity wasdivided by the forward velocity to give the coefficient of restitution.Shore hardness was determined in general accordance with ASTM Test 2240,but was measured on a non-dimpled area of the surface of the golf ball.

Comparative Example 1 Ionic Copolymer Cover (Non-Terpolymer)

A set of 12 two-piece golf balls was made according to the sameprocedure as that of Example 1 with the exception that Nucrel® 925, anon-acrylate ester-containing acid copolymer was substituted for Nucrel®035. The resulting golf ball cover was too hard, resulting in fourbreaks during cold crack testing. The results are shown on Table 13.

Comparative Example 2 Ionomer—Ion-Ionic Terpolymer Blend

The procedure of Example 1 was repeated with the exception that the MgOMaster batch was replaced by pure Surlyn® 1605. All of the golf ballcovers broke during cold crack testing. The results are shown on Table13.

Comparative Example 3 Ionomer—Non-Ionic Copolymer Blend

The procedure of Comparative Example 1 was repeated with the exceptionthat the MgO master batch was replaced by pure Surlyn® 1605. The resultsare shown on Table 13. When subjected to cold crack testing, all of thegolf ball covers broke.

As can be seen from the results of Example 1 and Comparative Examples1-3, inferior golf balls are obtained when a hard, non-acrylateester-containing copolymer is used instead of a softer, acrylateester-containing terpolymer, and when either an acrylateester-containing acid terpolymer or a non-acrylate ester-containing acidcopolymer is not neutralized with metal ions.

TABLE 13 Experiment Cover PGA COR Shore C Cold No. Material Weight Comp.(×1000) Hardness Crack 1-1 75% Nucrel ® 035/ 45.2 104 .783 80 No breaks25% MgO MB in Surlyn ® 1605 Comp. 1 75% Nucrel ® 925/ 45.1 111 .798 90 4breaks 25% MgO MB in Surlyn ® 1605 Comp. 2 75% Nucrel ® 035/ 45.1 99.774 70 All broke 25% Surlyn ® 1605 Comp. 3 75% Nucrel ® 925/ 45.2 106.790 75 All broke 25% Surlyn ® 1605

Example 2 Ionic Terpolymers

An acrylate ester-containing terpolymer sold as Escor® ATX 325 (ExxonChemical Co.) was 57% neutralized with lithium cations. The ionomericmaterial, which also contained titanium dioxide, brightener, etc. from awhite master batch, was placed over a solid golf ball core and the golfball was primed and top coated. The properties of the resulting golfball are shown on Table 14. This procedure was repeated using differentcombinations of terpolymers with cations and cation blends at thedegrees of neutralization which are shown on Table 14. In the cationblends, mole ratios were about 1:1:1. All of the ATX materials shown onTable 14 are Escor® ATX materials available from Exxon Chemical Co. TheNucrel® materials are available from DuPont Chemical Co. Primacor® 3440is available from Dow Chemical Co.

The spin rate of the golf ball was measured by striking the resultinggolf balls with a pitching wedge or 9-iron wherein the club-head speedis about 80 feet per second and the ball was launched at an angle of 26to 34 degrees with an initial velocity of 100-115 feet per second. Thespin rate was measured by observing the rotation of the ball in flightusing stop action Strobe photography or via the use of a high speedvideo system.

The scuff resistance test was conducted in the following manner: aTop-Flite® tour pitching wedge (1994) with box grooves was obtained andwas mounted in a Miyamae® driving machine. The club face was orientedfor a square hit. The forward/backward tee position was adjusted so thatthe tee was four inches behind the point in the downswing where the clubwas vertical. The height of the tee and the toe-heel position of theclub relative to the tee were adjusted in order that the center of theimpact mark was about ¾ of an inch above the sole and was centered toeto heel across the face. The machine was operated at a club head speedof 125 feet per second. A minimum of three samples of each ball weretested. Each ball was hit three times.

After testing, the balls were rated according to the following table:

Rating Type of damage 1 Little or no damage (groove markings or dents) 2Small cuts and/or ripples in cover 3 Moderate amount of material liftedfrom ball surface but still attached to ball 4 Material removed orbarely attachedThe balls that were tested were primed and top coated.

As shown on Table 14, many of the cover materials resulted in golf ballshaving a scuff resistance of 1.5 or less, and others had a scuffresistance rating of 1.5-2.5.

Comparative Example 4 Hard/Soft Ionomer Blend

A golf ball with a cover formed from a blend of a commercially availablehard sodium ionomer and a commercially available soft acrylateester-containing zinc ionomer in which the blend contains less than 60wt % soft ionomer was subjected to the same testing as the golf balls ofExample 2. The results are shown on Table 14.

TABLE 14 Spin Rate Experiment % PGA COR Shore D Scuff (#9 Iron at No.Cover Material Cation Neutralization Comp. (×1000) Hardness Resist. 105ft/sec) Comp. 4 Hard-soft ionomer Zn/Na 60 90 787 58 4.0 9,859 blend 1(control) 2-1 ATX 325 Li 57 86 787 51 1.0 10,430 2-2 ATX 325 Li/Zn/K 6586 787 50 1.0 10,464 2-3 ATX 320 Li 57 N.T. N.T. 56 1.0 10,299 2-4 ATX320 Li/Zn/K 65 87 790 55 1.5 10,355 2-5 Nucrel 010 Li — 89 803 65 3.07,644 2-6 Nucrel 010 Li/Zn/K — 89 802 65 4.0 7,710 2-7 Nucrel 035 Li —87 801 62 3.0 8,931 2-8 Nucrel 035 Li/Zn/K — 87 798 62 3.0 8,915 2-9 ATX310 Li 53 88 802 62 2.5 8,892 2-10 ATX 310 Li/Zn/K 60 88 801 63 2.58,244 2-11 ATX 325 Li 57 83 797 55 1.5 — 2-12 ATX 325 Li/Zn/K 65 82 79653 1.5 — 2-13 50% ATX 325-Li Li   28.5 89 777 50 1.5 — 50% ATX 320-unneut. 2-14 75% ATX320- Li/Zn/K 49 87 776 54 1.5 — Li/Zn/K 25% ATX320-unneut. 2-15 60% ATX325 Li/Zn/K 39 88 779 54 1.5 — 40% Primacor3440-unneut. 2-16 ATX 320 Unneut. — 88 775 45 2.0 — 2-17 ATX 325 Unneut.— 88 — 42 1.5 — 2-18 ATX 325 Li 50 95 795 50 1.0 — 2-19 ATX 325 Li 30 96791 46 1.5 — 2-20 ATX 325 Li/Zn/K 50 91 791 48 1.0 — 2-21 ATX 325Li/Zn/K 30 90 N.T. 45 1.0 — 2-22 ATX 325 Li/Zn/K 50 91 N.T. 47 1.0 —

Example 3 Ionic Terpolymers

The procedure of Example 2 was repeated with the exception that singlecations of lithium, magnesium, sodium and potassium were used in thecover material. The results are shown on Table 15.

As indicated on Table 15, the scuff resistance of the golf balls was 3.0or better. The scuff resistance of the balls with covers made of anacrylic acid terpolymer was 1.0. For a given terpolymer, the scuffresistance did not change when different cations were used forneutralization.

TABLE 15 Experiment Cover PGA COR Shore D Scuff No. Material Cation %Neutralization Comp. (×1000) Hardness Resistance 3-1 Nucrel ® 035 Li 10090 792 62 3.0 3-2 Nucrel ® 035 Mg 100 89 792 62 3.0 3-3 ATX 325 Li 10086 790 51 1.0 3-4 ATX 325 Mg 100 85 791 51 1.0 3-5 ATX 325 Na 81 85 79051 1.0 3-6 ATX 325 K 95 85 791 51 1.0

Comparative Example 5

Several intermediate balls (cores plus inner cover layers) were preparedin accordance with conventional molding procedures described above. Theinner cover compositions were molded around 1.545 inch diameter coresweighing 36.5 grams with a specific gravity of about 1.17 such that theinner cover had a wall thickness of about 0.0675 inches and a specificgravity of about 0.95, with the overall ball measuring about 1.680inches in diameter.

The cores utilized in the examples were comprised of the followingingredients: 100 parts by weight high cis-polybutadiene, 31 parts byweight zinc diacrylate, about 6 parts by weight zinc oxide, 20 parts byweight zinc stearate, 17-18 parts by weight calcium carbonate, and smallquantities of peroxide, coloring agent and a polymeric isocyanate soldas Papi® 94 (Dow Chemical Co.). The molded cores exhibited PGAcompressions of about 100 and C.O.R. values of about 0.800.

The inner cover compositions designated herein as compositions A-Eutilized to formulate the intermediate balls are set forth in Table 16below. The resulting molded intermediate balls were tested to determinethe individual compression (Riehle), C.O.R., Shore C hardness, spin rateand cut resistance properties. These results are also set forth in Table16 below.

The data of these examples are the average of twelve intermediate ballsproduced for each example. The properties were measured according to thefollowing parameters:

Cut resistance was measured in accordance with the following procedure:A golf ball was fired at 135 feet per second against the leading edge ofa pitching wedge wherein the leading edge radius is 1/32 inch, the loftangle is 51 degrees, the sole radius is 2.5 inches and the bounce angleis 7 degrees.

The cut resistance of the balls tested herein was evaluated on a scaleof 1 to 5. The number 1 represents a cut that extends completely throughthe cover to the core. A 2 represents a cut that does not extendcompletely through the cover but that does break the surface. A 3 doesnot break the surface of the cover but does leave a permanent dent. A 4leaves only a slight crease which is permanent but not as severe as 3. A5 represents virtually no visible indentation or damage of any sort.

The spin rate of the golf ball was measured by striking the resultinggolf balls with a pitching wedge or 9 iron wherein the club head speedis about 105 feet per second and the ball is launched at an angle of 26to 34 degrees with an initial velocity of about 110 to 115 feet persecond. The spin rate was measured by observing the rotation of the ballin flight using stop action Strobe photography.

Initial velocity is the velocity of a ball when struck at a hammer speedof 143.8 feet per second in accordance with a test as prescribed by theU.S.G.A.

As will be noted, compositions A, B and C include high acid ionomericresins, With composition B further including zinc stearate. CompositionD represents the inner layer (i.e. Surlyn® 1605) used in U.S. Pat. No.4,431,193. Composition E provides a hard, low acid ionomeric resin.

The purpose behind producing and testing the balls of Table 16 was toprovide a subsequent comparison in properties with the multi-layer golfballs of the present invention.

TABLE 16 Molded Intermediate Golf Balls A B C D E Ingredients of InnerCover Compo- sitions Iotek ® 959 50 50 — — — Iotek ® 960 50 50 — — —Zinc Stearate — 50 — — — Surlyn ® — — 75 — — 8162 Surlyn ® — — 25 — —8422 Surlyn ® — — — 100 — 1605 Iotek ® — — — — 50 7030 Iotek ® — — — —50 8000 Properties of Molded Intermediate Balls Compression 58 58 60 6362 C.O.R. .811 .810 .807 .793 .801 Shore C 98 98 97 96 96 Hardness SpinRate 7,367 6,250 7,903 8,337 7,956 (R.P.M.) Cut 4-5 4-5 4-5 4-5 4-5Resistance

As shown in Table 16 above, the high acid ionomer resin inner coverlayer (molded intermediate balls A-C) have lower spin rates and exhibitsubstantially higher resiliency characteristics than the low acidionomer resin based inner cover layers of balls D and E.

Example 4

Multi-layer balls in accordance with the present invention were thenprepared. Specifically, the inner cover compositions used to produceintermediate golf balls from Table 16 were molded over the solid coresto a thickness of about 0.0375 inches, thus forming the inner layer. Thediameter of the solid core with the inner layer measured about 1.620inches. Alternatively, the intermediate golf balls of Table 16 wereground down using a centerless grinding machine to a size of 1.620inches in diameter to produce an inner cover layer of 0.0375 inches.

The size of 1.620 inches was determined after attempting to mold theouter cover layer to various sizes (1.600″, 1.610″, 1.620″, 1.630″ and1.640″) of intermediate (core plus inner layer) balls. It was determinedthat 1.620″ was about the largest “intermediate” ball (i.e., core plusinner layer) which could be easily molded over with the soft outer layermaterials of choice. The goal herein was to use as thin an outer layeras necessary to achieve the desired playability characteristics whileminimizing the cost of the more expensive outer materials. However, witha larger diameter final golf ball and/or if the cover is compressionmolded, a thinner cover becomes feasible.

With the above in mind, an outer cover layer composition was blendedtogether in accordance with conventional blending techniques. The outerlayer composition used for this portion of the example is a relativelysoft cover composition such as those listed in U.S. Pat. No. 5,120,791.An example of such a soft cover composition is a 45% soft/55% hard lowacid ionomer blend designated by the inventor as “TE-90”. Thecomposition of TE-90 is set forth as follows:

Outer Cover Layer Composition TE-90 Iotek ® 8000 22.7 weight % Iotek ®7030 22.7 weight % Iotek ® 7520 45.0 weight % White MB¹  9.6 weight %¹White MB consists of about 23.77 weight percent TiO₂; 0.22 weightpercent Uvitex ® OB, 0.03 weight percent Santonox ® R, 0.05 weightpercent Ultramarine Blue ™ and 75.85 weight percent Iotek ® 7030.

The above outer layer composition was molded around each of the 1.620diameter intermediate balls comprising a core plus one of compositionsA-D, respectively. In addition, for comparison purposes, Surlyn® 1855(new Surlyn® 9020), the cover composition of the '193 patent, was moldedabout the inner layer of composition D (the intermediate ballrepresentative of the '193 patent). The outer layer TE-90 was molded toa thickness of approximately 1.680 inches in diameter. The resultingballs (a dozen for each example) were tested and the various propertiesthereof are set forth in Table 17 as follows:

TABLE 17 Finished Balls 1 2 3 4 5 Ingredients: Inner Cover A B C D DComposition Outer Cover TE-90 TE-90 TE-90 TE-90 Surlyn ® Composition9020 Properties of Molded Finished Balls: Compression 63 63 69 70 61C.O.R. .784 .778 .780 .770 .757 Shore C 88 88 88 88 89 Hardness Spin8,825 8,854 8,814 8,990 8,846 (R.P.H.) Cut 3-4 3-4 3-4 3-4 1-2Resistance

As it will be noted in finished balls 1-4, by creating a multi-layercover utilizing the high acid ionomer resins in the inner cover layerand the hard/soft low acid ionomer resin in the outer cover layer,higher compression and increased spin rates are noted over the singlelayer covers of Table 16. In addition, both the C.O.R. and the Shore Chardness are reduced over the respective single layer covers of Table16. This was once again particularly true with respect to themulti-layered balls containing the high acid ionomer resin in the innerlayer (i.e. finished balls 1-5). In addition, with the exception ofprior art ball 5 (i.e. the '193 patent), resistance to cutting remainsgood but is slightly decreased.

Furthermore, it is also noted that the use of the high acid ionomerresins as the inner cover material produces a substantial increase inthe finished balls overall distance properties. In this regard, the highacid ionomer resin inner covers of balls 1-3 produce an increase ofapproximately 10 points in C.O.R. over the low acid ionomer resin innercovers of balls 4 and about a 25 point increase over the prior art balls5. Since an increase in 3 to 6 points in C.O.R. results in an averageincrease of about 1 yard in distance, such an improvement is deemed tobe significant.

Several other outer layer formulations were prepared and tested bymolding them around the core and inner cover layer combination to formballs each having a diameter of about 1.68 inches. First, B.F. GoodrichEstane® X-4517 polyester polyurethane was molded about the core moldedwith inner layer cover formulation A. DuPont Surlyn® 9020 was moldedabout the core which was already molded with inner layer D. Similarproperties tests were conducted on these golf balls and the results areset forth in Table 18 below:

TABLE 18 Finished Balls 6 7 Ingredients: Inner Cover Layer A DComposition Outer Cover Layer Estane ® 4517 Surlyn ® 9020 CompositionProperties of Molded Finished Balls: Compression 67 61 C.O.R. .774 .757Shore C Hardness 74 89 Spin (R.P.M.) 10,061 8,846 Cut Resistance 3-4 1-2

The ball comprising inner layer formulation D and Surlyn® 9020identifies the ball in the Nesbitt U.S. Pat. No. 4,431,193. As is noted,the example provides for relatively high softness and spin rate thoughit suffers from poor cut resistance and low C.O.R. This ball isunacceptable by today's standards.

As for the Estane® X-4517 polyester polyurethane, a significant increasein spin rate over the TE-90 cover is noted along with an increase inspin rate over the TE-90 cover is noted along with an increasedcompression. However, the C.O.R. and Shore C values are reduced, whilethe cut resistance remains the same. Furthermore, both the Estane®X-4517 polyester polyurethane and the Surlyn® 9020 were relativelydifficult to mold in such thin sections.

Example 5

In order to analyze the change in characteristics produced bymulti-layer golf balls (standard size) having inner cover layerscomprised of ionomer resin blends of different acid levels, a series ofexperiments was run. A number of tests were performed, varying the typeof core, inner cover layer and outer cover layer. The results are shownbelow on Table 19:

TABLE 19 Inner Comp/ Outer COMP Sample # Core Layer Thickness COR CoverThickness (Rhiele) COR Shore D Spin 8 1042 None — See Below Top 0.055″61 .800 68 7331 Yellow Grade 9 1042 None — See Below 959/960 0.055″ 56.808 73 6516 Yellow 10 Special 959/960 0.050″ 65/.805 959/960 0.055″ 48.830 73 6258 1.47″ 11 1042 None — See Below SD 90 0.055″ 62 .792 6538421 Yellow 12 Special Top 0.050″ 66/.799 SD 90 0.055″ 55 .811 63 82651.47″ Grade 13 Special 959/960 0.050″ 65/.805 SD 90 0.055″ 53 .813 638254 1.47″ 14 Special Top 0.050″ 66/.799 Top 0.055″ 51 .819 68 73901.47″ Grade Grade 15 1042 None 0.050″ See Below Z-Balata 0.055″ 67 .78255 9479 Yellow 16 Special 959/960 0.050″ 65/.805 Z-Balata 0.055″ 61 .80055 9026 1.47″ 17 Special Top 0.050″ 66/.799 Z-Balata 0.055″ 60 .798 559262 1.47″ Grade 1042 Yellow Comp = 72, COR = .780 Special 1.47″ CORE >COMP = 67, COR = .782

In this regard, “Top Grade” or “TG” is a low acid inner cover ionomerresin blend comprising of 70.6% Iotek® 8000, 19.9% Iotek® 7010 and 9.6%white master batch. “959/960” is a 50/50 wt/wt blend of Iotek® 959/960.In this regard, Escor® or Iotek® 959 is a sodium ion neutralizedethylene-acrylic neutralized ethylene-acrylic acid copolymer. Accordingto Exxon, Ioteks® 959 and 960 contain from about 19.0 to about 21.0% byweight acrylic acid with approximately 30 to about 70 percent of theacid groups neutralized with sodium and zinc ions, respectively. Thephysical properties of these high acid acrylic acid based ionomers areas follows:

TABLE 20 ESCOR ® ESCOR ® PROPERTY (IOTEK ®) 959 (IOTEK ®) 960 Melt Indexg/10 min 2.0 1.8 Cation Sodium Zinc Melting Point, ° F. 172 174 VicatSoftening Point, ° F. 130 131 Tensile @ Break, psi 4600 3500 Elongation@ Break, % 325 430 Hardness, Shore D 66 57 Flexural Modulus, psi 66,00027,000

Furthermore, the low acid ionomer formulations for “SD 90” and“Z-Balata” are set forth below:

TABLE 21 SD Cover ZB Cover 17.2% Surlyn ® 8320   19% Iotek ® 8000  7.5%Surlyn ® 8120   19% Iotek ® 7030   49% Surlyn ® 9910 52.5% Iotek ® 752016.4% Surlyn ® 8940  9.5% white MB ®  9.7% white MB ®

The data clearly indicates that higher C.O.R. and hence increase traveldistance can be obtained by using multi-layered covered balls versusballs covered with single layers. However, some sacrifices incompression and spin are also noted. Further, as shown in comparingExample Nos. 12 vs. 13, Example Nos. 17 vs. 16, etc. use of lower acidlevel inner cover layers and relatively soft outer cover layers (i.e.,50 wt. % or more soft ionomer) produces softer compression and higherspin rates than the golf balls comprised of high acid inner coverlayers. Consequently, use of blends of low acid ionomer resins toproduce the inner layer of a multi-layer covered golf ball, produces notonly enhanced travel distance but also enhanced compression and spinproperties.

Example 6

Multi-layer oversized golf balls were produced utilizing differentionomer resin blends as the inner cover layer (i.e., core plus innercover layer is defined as “mantle”). The “ball data” of the oversizedmulti-layer golf balls in comparison with production samples of“Top-Flite® XL” and Top-Flite® Z-Balata” is set forth below.

The results indicate that use of multi-layer covers enhances C.O.R. andtravel distance. Further, the data shows that use of a blend of low acidionomer resins (i.e., “Top Grade”) to form the inner cover layer incombination with a soft outer cover (“ZB” or “SD”) produces enhancedspin and compression characteristics. The overall combination results ina relatively optimal golf ball with respect to characteristics of traveldistance, spin and durability.

Example 7

Golf balls 7-1, 7-2, 7-3 and 7-4 having the formulations shown on Table22 were formed.

TABLE 22 Chemical Component 7-1 7-2 7-3 7-4 Core Data Size 1.47″ 1.47″1.47″ 1.47″ Weight 32.7 g 32.7 g 32.7 g 32.7 g PGA Compression 70 60 7060 COR .780 .770 .780 .770 Composition High Cis polybutadiene 100 100100 100 Zinc oxide 30.5 31.6 30.5 31.6 Core regrind 16 16 16 16 Zincstearate 16 16 16 16 Zinc diacrylate 22 20 22 20 Initiator 0.9 0.9 0.90.9 Inner Cover Layer Size 1.57″ 1.57″ 1.57″ 1.57″ Weight 38.04 g 38.4 g38.4 g 38.4 g PGA Compression 83 75 83 75 COR .801 .795 .801 .795Thickness 0.050″ 0.050″ 0.050″ 0.050″ Hardness (Shore C/D) 97/70 97/7097/70 97/70 Composition Iotek ® 1002 50% 50% 50% 50% Iotek ® 1003 50%50% 50% 50% Outer Cover Layer Hardness (Shore C/D) 71/46 71/46 71/4671/46 Thickness 0.055″ 0.055″ 0.055″ 0.055″ Composition Iotek ® 751092.8%   92.8%   42% 42% Iotek ® 7520 42% 42% Iotek ® 7030 7.2%  7.2% 7.3%  7.3%  Iotek ® 8000 8.7%  8.7%  Whitener Package Unitane ™ 0-110 2.3 phr   2.3 phr  2.3 phr  2.3 phr Eastobrite ® OB1 0.025 phr 0.025phr. 0.025 phr 0.025 phr Ultra Marine Blue ™ 0.042 phr 0.042 phr  0.042phr 0.042 phr Santonox ® 0.004 phr 0.004 phr  0.004 phr 0.004 phr FinalBall Data Size 1.68″ 1.68″ 1.68″ 1.68″ Weight 45.4 g 45.4 g 45.4 g 45.4g PGA Compression 85 78 85 78 COR .793 .785 .793 .785

The balls of Example 7-2 were tested by a number of professional qualitygolfers using a driver, 5-iron, 9-iron, and sand wedge or pitchingwedge. Each player used his own clubs and hit both the ball of Example7-2 and a control ball, which was the 1995 two-piece Top-Flite® TourZ-balata 90. The Z-balata 90 has a 1.545″ core of about 36.8 g with aPGA compression of about 80 and a COR of about 0.794. The cover of theZ-balata 90 is about 0.068 in. thick, and is a blend of Iotek® 8000 andIotek® 7510 with or without master batch containing Iotek® 7030. Thecover has a shore D hardness of about 55. The ball has a PGA compressionof about 79 and a COR of about 0.788. Each player hit six of the ballsof Example 7-2 and six Z-balata control balls one time each. For eachshot, measurements were made of the initial launch conditions of thegolf ball, including launch angle and ball speed. Furthermore, spinrates at initial launch, carry distance, and total distance weremeasured. The players hit full shots with the driver (1W), 5-iron (5I)and 9-iron (9I). With the sand wedge or pitching wedge (SW), the playershit about 30 yard chip shots. Data points were removed if determined tobe “wild points.” A point was said to be wild if it fell outside 2standard deviations of the 6-hit average. Initial launch conditions weredetermined using a highly accurate high speed stop action videophotography system. The results are shown on Table 23.

As shown on Table 23, multi-layer ball 7-2 was longer than the Z-balatacontrol when hit with a 5-iron but only slightly longer than theZ-balata ball using a driver and 9-iron. The multi-layer ball 7-2 andthe two-piece control were generally the same in overall distance usinga driver. In each case, the multi-layer ball 7-2 had a higher spin rateoff the 30-yard chip shot than the Z-balata. The spin rate of the ballof Example 7-2 was an average of 11.6% higher than the spin rate of theZ-balata control in the 30 yard chip shot.

TABLE 23 2-Piece Control 7-2 L.A. B.S. Spin Carry Total L.A. Spin CarryTotal Player Club (deg) (fps) (rpm) (yds) (yds) (deg) (rpm) (yds) (yds)B.S. (fps) 1 1W 10.4 262.2 3537 272.5 288.9 10.0 262.3 3247 271.6 292.22 1W 9.5 240.1 3124 238.1 253.6 8.9 238.3 2935 236.3 257.4 3 1W 8.6258.8 3695 254.1 259.9 6.3 251.2 3357 247.6 260.8 4 1W 10.9 252.6 2639271.6 289.8 12.5 251.4 3066 279.0 296.7 5 1W 9.5 211.7 3627 237.2 255.29.4 208.7 3415 235.0 259.8 6 1W 10.2 242.0 3105 263.8 283.2 11.0 243.92903 267.6 288.4 7 1W 11.5 214.9 3089 265.4 279.0 11.6 212.6 3165 262.9274.4 8 1W 9.7 239.5 3129 263.6 28.8 9.3 235.3 2884 257.2 276.8 9 1W11.7 211.2 2939 231.4 255.8 11.3 208.5 2032 222.2 244.3 10  1W 10.2244.0 2797 243.3 250.2 9.7 239.6 3072 236.8 251.1 11  1W 247.4 263.813.8 215.8 3916 245.4 268.8 Ave. 10.2 237.7 3168 253.5 269.8 10.3 233.43090 251.1 270.1 1 5I 12.4 207.3 5942 198.3 209.8 11.8 206.3 5507 196.2207.8 2 5I 178.3 184.2 14.9 199.4 5094 182.2 187.8 3 5I 10.9 196.8 6462185.2 188.9 11.5 197.0 6009 187.4 193.4 4 5I 14.4 205.5 6683 207.8 213.714.7 208.3 6601 207.5 217.8 5 5I 13.6 183.3 6734 182.9 189.4 14.2 180.96380 184.2 190.7 6 5I 12.4 204.5 5771 201.0 210.5 12.9 208.4 5414 208.0218.3 7 5I 14.1 184.3 6013 194.8 198.1 13.1 182.7 6000 192.9 200.0 8 5I12.8 187.2 6149 188.0 200.3 13.1 191.6 6183 191.7 202.0 9 5I 13.2 176.56000 168.2 173.7 13.6 172.5 6166 169.7 174.3 10  5I 13.9 199.9 7214175.2 178.2 14.9 199.1 6237 169.0 170.2 11  5I 14.2 179.5 6669 181.9187.8 15.7 181.2 5338 184.0 190.7 Ave. 13.2 192.5 6364 187.4 194.1 13.7193.4 5903 188.4 195.7 B.S. (deg) 1 9I 20.0 168.1 9865 152.5 159.5 20.4172.2 9210 153.4 159.6 2 9I 21.8 165.9 9770 132.7 137.0 23.0 164.7 8949132.7 134.6 3 9I 19.9 154.3 10764 128.8 134.3 19.9 156.5 1061 129.8135.0 4 9I 22.7 166.4 10551 146.0 148.8 23.9 165.7 9990 150.3 154.2 5 9I22.1 147.4 9682 137.1 138.1 22.2 148.5 9324 139.3 141.7 6 9I 19.4 169.78939 153.3 158.0 19.7 168.2 8588 156.2 163.5 7 9I 20.4 151.1 9899 147.5150.0 21.6 150.3 9084 148.6 151.3 8 9I 18.5 143.0 9408 142.0 147.5 18.3141.8 9038 141.2 144.8 9 9I 20.0 134.5 9124 124.9 128.8 20.1 132.9 8834125.0 128.9 10  9I 23.2 156.1 10603 122.7 124.1 23.2 155.6 11017 116.2116.3 11  9I 21.5 149.4 9729 131.0 134.5 23.4 151.7 8686 133.3 136.8Ave. 20.9 155.1 9849 138.0 141.9 21.4 155.3 9353 138.7 142.4 1 SW 29.256.4 5647 24.8 58.9 6679 2 SW 26.6 57.4 5446 25.2 57.8 5647 3 SW 25.864.1 4925 24.3 63.5 5550 4 SW 30.9 60.9 5837 31.1 57.9 6158 5 SW 20.356.7 4152 19.0 56.3 4288 6 SW 34.3 57.1 3798 32.4 61.5 4700 7 SW 30.551.5 4712 29.3 52.3 5374 Ave. 28.2 67.7 4931 26.6 58.3 6485

Example 8

The ball of Example 7-2 was compared to a number of competitive productsin distance testing using a driving machine in which the ball was struckwith a club. The results are shown on Table 24 below. The distance testshows that Example 7-2 is about the same distance as the Z-balata 90control and longer than the Titleist® HP-2 Tour (soft covered two-piece)and Titleist® Tour Balata 100 ball (Balata covered wound ball). Theother balls that were tested include the Maxfli® (Dunlop) XS100, Maxfli®(Dunlop) XF100, and the GIGA Top-Flite® golf ball sold by Spalding inJapan. In Table 24, the ball of Example 7-2 is the longest ball.

TABLE 24 Distance Report Test Number: 131951 Club Head Speed: 157.35Club Name: TFT 10.5 DEG MW (Driver) No. Balls/Type: 10 Average TestConditions: Launch Angels (Deg.): 9.6 Ball Speed (fps): 217.9 Spin Rate(rpm): 3390 Turf Condition: FIRM Wind (mph/dir): 2.55 135.20 Temp/RH(deg/%): 0.61 91.59 P-Bar (mbar): 1015 Ball Type Traj PTime Carry CarDiff Ctr Dev Roll T Dist T Diff HP2TOUR 8.7 6.0 230.4 −4.1 3.0 9.9 240.3−4.3 ZB90 9.0 6.1 231.8 −2.7 5.4 9.1 241.0 −3.6 GIGA 8.8 6.0 234.5 0.05.7 10.2 244.6 0.0 Example 7-2 8.3 5.9 229.6 −4.9 3.8 11.1 240.7 −3.9Titleist Tour Balata 100 9.2 6.2 229.2 −5.3 7.8 7.8 236.9 −7.7 TestNumber: 0203963 Club Head Speed: 126.18 Club Name: TFT 5 IRON No.Balls/Type: 12 Average Test Conditions: Launch Angels (Deg.): 14 BallSpeed (fps): 180.1 Spin Rate (rpm): 5424 Turf Condition: FIRM Wind(mph/dir): 6.23 171.38 Temp/RH (deg/%): 62.20 98.16 P-Bar (mbar): 1015Ball Type Traj PTime Carry Car Diff Ctr Dev Roll T Dist T Diff HP2TOUR25.3 6.0 156.0 −7.4 −3.0 1.5 157.5 −9.5 ZB90 25.2 6.0 157.1 −6.3 −3.32.2 159.3 −7.7 GIGA 25.0 6.0 162.2 −1.2 −3.1 2.9 165.1 −1.9 Example 7-223.5 6.0 163.4 0.0 −3.3 3.7 167.0 0.0 Titleist Tour Balata 100 23.9 6.0158.7 −4.7 −2.3 2.5 161.2 −5.8 ZB 100 26.1 6.0 155.6 −7.8 −4.5 2.0 157.6−9.4 XS 100 23.9 6.0 161.3 −2.3 −5.6 2.6 163.9 −3.1 XF 100 24.5 6.0152.0 −11.4 −6.2 1.6 153.7 −13.3

Example 9

A number of golf ball cores having the following formulation were made:

PARTS High-cis polybutadiene 100 Zinc oxide 30 Core regrind 16 Zincstearate 16 Zinc diacrylate 21 Peroxide (231 xl) 0.9The cores had a diameter of 1.470″, a weight of 32.5 g, a PGAcompression of 57 and a COR of 0.768.

The cores were divided into four sets and each set was covered with oneof the mantle formulations shown below in Table 25.

TABLE 25 MANTLE FORMULATIONS Mantle Type A B C D (control) Surlyn ® 8940(g) 656 880 1610 — Surlyn ® 9910 (g) 1964 2180 535 — Surlyn ® 8120 (g)300 160 475 — Surlyn ® 8320 (g) 700 400 1000 — Iotek ® 7030 (g) 380 380380 — Iotek ® 1002 (g) — — — 2000 Iotek ® 1003 (g) — — — 2000

The mantle covered cores had the following physical properties:

TABLE 26 MANTLE-COVERED CORES A B C D Size (Pole) (Inches) 1.577 1.5761.572 1.573 Weight (g) 38.6 38.5 38.3 38.4 PGA Compression 71 74 70 76COR .7795 .7831 .7768 .7946 Std. Dev. COR .0051 .0026 .0016 .0012 ShoreC 92 94 90 97 Shore D 62 65 61 70

Each set of mantle-covered cores was divided into three subsets and acover layer having one of the cover formulations shown below on Table 27was formed over the mantled cores. The “whitener package” on Table 27consists of White MB, the composition of which was previously describedherein.

TABLE 27 COVER FORMULATIONS Cover Type X Y Z Iotek ® 7520 (g) 1660 14801300 Iotek ® 7510 (g) 1660 1480 1300 Iotek ® 8000 (g) 304 664 1024Iotek ® 7030 (g) 282 282 282 Whitener package (g) 94 94 94

The balls had the mantle and cover combinations and properties shownbelow on Table 28.

TABLE 28 Ball Properties Example No. 9-1 9-2 9-3 9-4 9-5 9-6 9-7 9-8 9-99-10 9-11 9-12 Mantle A A A B B B C C C D D D Cover X Y Z X Y Z X Y Z XY Z Size 1.682 1.681 1.682 1.682 16.82 1.682 1.682 1.682 1.681 1.6821.682 1.681 (inch) Weight 45.68 45.57 45.58 45.77 45.62 45.58 45.6345.58 45.48 45.67 45.65 45.57 (g) PGA 73.5 74.3 74.7 77.4 76.7 76.3 70.871.9 73.3 79.5 80 82.5 Comp. COR .7639 .7665 .7680 .7701 .7703 .7704.7607 .7630 .7661 .7771 .7798 .7839 Std. .0041 .0027 .0037 .0077 .0034.0023 .0037 .0030 .0028 .0034 .0028 .0020 Dev. COR Shore C 71 76 81 7176 81 70 76 80 71 76 81 Shore D 46 50 53 46 50 53 46 49 52 47 41 53Ball 9-10 was the control.

The results from Table 28 demonstrate that a multi-layer ball having amantle hardness of 60D or greater (Ex. 9-7, 9-8, 9-9), and preferably63D (Ex. 9-1, 9-2, 9-3) or greater give a ball having a COR of at least0.761 (Ex. 9-7) and while a harder mantle (Ex. (9-4, 9-5, 9-6, 9-10,9-11, 9-12) will generally give higher COR, it also contributes to aharder PGA compression. Versus the control ball (Ex. 9-10) it isdemonstrated that softer compressions can be obtained with slightlysofter mantles while maintaining a good COR. Likewise versus thecontrol, higher COR balls may be designed (Ex. 9-11, 9-12) that stillhave a relatively soft compression for good feel.

Example 10

A number of golf balls were made having the core and cover formulationsand the physical properties shown on Tables 29 and 30. The balls ofExamples 10-1, 10-2 and 10-5 are part of the invention. The balls ofExamples 10-3, 10-4 and 10-6 are controls based upon the cover layerchemistry of comparative Example 2 of U.S. Pat. No. 5,586,950. The ballsof Example 10-4 are replicas of comparative Example 2 of U.S. Pat. No.5,586,950.

For all of the balls, the cores were molded and centerless ground to theappropriate size. The mantles of Examples 10-1 to 10-4 were injectionmolded in a 1.63″ injection mold. The mantles for the balls of Examples10-5 and 10-6 also were injection molded. All of the outer cover layerswere injection molded.

TABLE 29 Core Data Ex. 10-1 Ex. 10-2 Ex. 10-3 Ex. 10-4 Ex. 10-5 Ex. 10-6Core Types (See Table 2) A A A A B B Mantle Data 1.50 1.50 1.50 1.501.47 1.47 Ingredients phr phr phr phr phr phr Iotek ® 1002 50 — 50 — 5050 Iotek ® 1003 50 — 50 — 50 50 Surlyn ® 9910 — 50 — 50 — — Surlyn ®8940 — 35 — 35 — — Surlyn ® 8920 — 15 — 15 — — TiO₂ 2 2 2 2 — — Diameter(in.) 1.625 1.625 1.625 1.625 1.57 1.57 Thickness (in.) 0.063 0.0630.063 0.063 0.050 0.050 Shore C/D Hardness 97/70 96/68 97/70 96/68 97/7097/70 (measured on ball) Cover Data Cover Type (see Table 2) #1 #1 #2 #2#1 #2 Size (in.) 1.70 1.70 1.70 1.70 1.68 1.68 Thickness (in.) 0.0380.038 0.038 0.038 0.055 0.055 Shore C/D Hardness 75/49 75/49 84/57 83/5772/48 83/56 (measured on ball) Compression (Rhiele) 63 66 60 63 83 80COR .800 .795 .805 .798 .779 .787

TABLE 30 Core Formulations Cover Formulations Materials (phr) A BMaterials (phr) #1 #2 BR 1220 (High cis 73 70 Iotek ® 8000 8.5 —polybutadiene) Taktene ® 220 (High cis 27 30 Iotek ® 7510 41 —polybutadiene) Zinc Oxide 22.3 31.5 Iotek ® 7520 41 — TG Regrind 10 16Master batch C 9.5 — Zinc Stearate 20 16 Surlyn ® 1557 — 10 ZincDiacrylate 26 20 Surlyn ® 1855 — 20 Master batch A 0.15 — Surlyn ® 8265— 20 Master batch B — 0.15 Surlyn ® 8269 — 50 Luperco ® 231 XL peroxide0.9 0.9 TiO2 — 2

DEFINITIONS Coefficient of Restitution

As is apparent from the above discussions, two principal propertiesinvolved in golf ball performance are resilience and PGA compression.The resilience or coefficient of restitution (COR) of a golf ball is theconstant “e,” which is the ratio of the relative velocity of an elasticsphere after direct impact to that before impact. As a result, the COR(“e”) can vary from 0 to 1, with 1 being equivalent to a perfectly orcompletely elastic collision and 0 being equivalent to a perfectly orcompletely inelastic collision.

COR, along with additional factors such as club head speed, club headmass, ball weight, ball size and density, spin rate, angle of trajectoryand surface configuration (i.e., dimple pattern and area of dimplecoverage) as well as environmental conditions (e.g. temperature,moisture, atmospheric pressure, wind, etc.) generally determine thedistance a ball will travel when hit. Along this line, the distance agolf ball will travel under controlled environmental conditions is afunction of the speed and mass of the club and size, density andresilience (COR) of the ball and other factors. The initial velocity ofthe club, the mass of the club and the angle of the ball's departure areessentially provided by the golfer upon striking. Since club head, clubhead mass, the angle of trajectory and environmental conditions are notdeterminants controllable by golf ball producers and the ball size andweight are set by the U.S.G.A., these are not factors of concern amonggolf ball manufacturers. The factors or determinants of interest withrespect to improved distance are generally the coefficient ofrestitution (COR) and the surface configuration (dimple pattern, ratioof land area to dimple area, etc.) of the ball.

The COR of solid core balls is a function of the composition of the coreand of the cover. The core and/or cover may be comprised of one or morelayers such as in multi-layered balls. In balls containing a wound core(i.e., balls comprising a liquid or solid center, elastic windings, anda cover), the coefficient of restitution is a function of not only thecomposition of the center and cover, but also the composition andtension of the elastomeric windings. As in the solid core balls, thecenter and cover of a wound core ball may also consist of one or morelayers. The COR of the golf balls of the present invention is a functionof the composition and physical properties of the core and cover layermaterials such as flex modulus, hardness and particularly, theirresilience, i.e. ability to quickly recover from a high impactdeformation.

The coefficient of restitution is the ratio of the outgoing velocity tothe incoming velocity. In the examples of this application, thecoefficient of restitution of a golf ball was measured by propelling aball horizontally at a speed of 125±5 feet per second (fps) andcorrected to 125 fps against a generally vertical, hard, flat steelplate and measuring the ball's incoming and outgoing velocityelectronically. Speeds were measured with a pair of Oehler Mark 55ballistic screens available from Oehler Research, Inc., P.O. Box 9135,Austin, Tex. 78766, which provide a timing pulse when an object passesthrough them. The screens were separated by 36″ and are located 25.25″and 61.25″ from the rebound wall. The ball speed was measured by timingthe pulses from screen 1 to screen 2 on the way into the rebound wall(as the average speed of the ball over 36″), and then the exit speed wastimed from screen 2 to screen 1 over the same distance. The rebound wallwas tilted 2 degrees from a vertical plane to allow the ball to reboundslightly downward in order to miss the edge of the cannon that fired it.The rebound wall is solid steel 2.0 inches thick.

As indicated above, the incoming speed should be 125±5 fps but correctedto 125 fps. The correlation between COR and forward or incoming speedhas been studied and a correction has been made over the +5 fps range sothat the COR is reported as if the ball had an incoming speed of exactly125.0 fps.

The coefficient of restitution must be carefully controlled in allcommercial golf balls if the ball is to be within the specificationsregulated by the United States Golf Association (U.S.G.A.). As mentionedto some degree above, the U.S.G.A. standards indicate that a“regulation” ball cannot have an initial velocity exceeding 255 feet persecond in an atmosphere of 75° F. when tested on a U.S.G.A. machine.Since the coefficient of restitution of a ball is related to the ball'sinitial velocity, it is highly desirable to produce a ball havingsufficiently high coefficient of restitution to closely approach theU.S.G.A. limit on initial velocity, while having an ample degree ofsoftness (i.e., hardness) to produce enhanced playability (i.e., spin,etc.).

PGA Compression

PGA compression is another important property involved in theperformance of a golf ball. The compression of the ball can affect theplayability of the ball on striking and the sound or “click” produced.Similarly, compression can affect the “feel” of the ball (i.e., hard orsoft responsive feel), particularly in chipping and putting.

Moreover, while compression itself has little bearing on the distanceperformance of a ball, compression can affect the playability of theball on striking. The degree of compression of a ball against the clubface and the softness of the cover strongly influences the resultantspin rate. Typically, a softer cover will produce a higher spin ratethan a harder cover. Additionally, a harder core will produce a higherspin rate than a softer core. This is because at impact a hard coreserves to compress the cover of the ball against the face of the club toa much greater degree than a soft core thereby resulting in more “grab”of the ball on the clubface and subsequent higher spin rates. In effectthe cover is squeezed between the relatively incompressible core andclubhead. When a softer core is used, the cover is under much lesscompressive stress than when a harder core is used and therefore doesnot contact the clubface as intimately. This results in lower spinrates. The term “compression” utilized in the golf ball trade generallydefines the overall deflection that a golf ball undergoes when subjectedto a compressive load. For example, PGA compression indicates the amountof change in golf ball's shape upon striking.

In the past, PGA compression related to a scale of from 0 to 200 givento a golf ball. The lower the PGA compression value, the softer the feelof the ball upon striking. In practice, tournament quality balls havecompression ratings around 70-110, preferably around 80 to 100.

In determining PGA compression using the 0-200 scale, a standard forceis applied to the external surface of the ball. A ball which exhibits nodeflection (0.0 inches in deflection) is rated 200 and a ball whichdeflects 2/10th of an inch (0.2 inches) is rated 0. Every change of0.001 of an inch in deflection represents a 1 point drop in compression.Consequently, a ball which deflects 0.1 inches (100×0.001 inches) has aPGA compression value of 100 (i.e., 200−100) and a ball which deflects0.110 inches (110×0.001 inches) has a PGA compression of 90 (i.e.,200−110).

In order to assist in the determination of compression, several deviceshave been employed by the industry. For example, PGA compression isdetermined by an apparatus fashioned in the form of a small press withan upper and lower anvil. The upper anvil is at rest against a 200-pounddie spring, and the lower anvil is movable through 0.300 inches by meansof a crank mechanism. In its open position the gap between the anvils is1.780 inches allowing a clearance of 0.100 inches for insertion of theball. As the lower anvil is raised by the crank, it compresses the ballagainst the upper anvil, such compression occurring during the last0.200 inches of stroke of the lower anvil, the ball then loading theupper anvil which in turn loads the spring. The equilibrium point of theupper anvil is measured by a dial micrometer if the anvil is deflectedby the ball more than 0.100 inches (less deflection is simply regardedas zero compression) and the reading on the micrometer dial is referredto as the compression of the ball. In practice, tournament quality ballshave compression ratings around 80 to 100 which means that the upperanvil was deflected a total of 0.120 to 0.100 inches.

An example to determine PGA compression can be shown by utilizing a golfball compression tester produced by Atti Engineering Corporation ofNewark, N.J. The value obtained by this tester relates to an arbitraryvalue expressed by a number which may range from 0 to 100, although avalue of 200 can be measured as indicated by two revolutions of the dialindicator on the apparatus. The value obtained defines the deflectionthat a golf ball undergoes when subjected to compressive loading. TheAtti test apparatus consists of a lower movable platform and an uppermovable spring-loaded anvil. The dial indicator is mounted such that itmeasures the upward movement of the springloaded anvil. The golf ball tobe tested is placed in the lower platform, which is then raised a fixeddistance. The upper portion of the golf ball comes in contact with andexerts a pressure on the springloaded anvil. Depending upon the distanceof the golf ball to be compressed, the upper anvil is forced upwardagainst the spring.

Alternative devices have also been employed to determine compression.For example, Applicant also utilizes a modified Riehle CompressionMachine originally produced by Riehle Bros. Testing Machine Company,Phil., PA to evaluate compression of the various components (i.e.,cores, mantle cover balls, finished balls, etc.) of the golf balls. TheRiehle compression device determines deformation in thousandths of aninch under a load designed to emulate the 200 pound spring constant ofthe Atti or PGA compression testers. Using such a device, a Riehlecompression of 61 corresponds to a deflection under load of 0.061inches.

Additionally, an approximate relationship between Riehle compression andPGA compression exists for balls of the same size. It has beendetermined by Applicant that Riehle compression corresponds to PGAcompression by the general formula PGA compression=160-Riehlecompression. Consequently, 80 Riehle compression corresponds to 80 PGAcompression, 70 Riehle compression corresponds to 90 PGA compression,and 60 Riehle compression corresponds to 100 PGA compression. Forreporting purposes, Applicant's compression values are usually measuredas Riehle compression and converted to PGA compression.

Furthermore, additional compression devices may also be utilized tomonitor golf ball compression so long as the correlation to PGAcompression is know. These devices have been designed, such as a WhitneyTester, to correlate or correspond to PGA compression through a setrelationship or formula.

Shore D Hardness

As used herein, “Shore D hardness” of a cover is measured generally inaccordance with ASTM D-2240, except the measurements are made on thecurved surface of a molded cover, rather than on a plaque. Furthermore,the Shore D hardness of the cover is measured while the cover remainsover the core. When a hardness measurement is made on a dimpled cover,Shore D hardness is measured at a land area of the dimpled cover.

Fillers

In a particularly preferred form of the invention, at least one layer ofthe golf ball contains at least 0.01 parts by weight of a filler.Fillers preferably are used to adjust the density, flex modulus, moldrelease, and/or melt flow index of a layer. More preferably, at leastwhen the filler is for adjustment of density or flex modulus of a layer,it is present in an amount of at least five parts by weight based upon100 parts by weight of the layer composition. With some fillers, up toabout 200 parts by weight probably can be used.

A density adjusting filler according to the invention preferably is afiller which has a specific gravity which is at least 0.05 and morepreferably at least 0.1 higher or lower than the specific gravity of thelayer composition. Particularly preferred density adjusting fillers havespecific gravities which are higher than the specific gravity of theresin composition by 0.2 or more, even more preferably by 2.0 or more.

A flex modulus adjusting filler according to the invention is a fillerwhich, when used in an amount of e.g. 1-100 parts by weight based upon100 parts by weight of resin composition, will raise or lower the flexmodulus (ASTM D-790) of the resin composition by at least 1% andpreferably at least 5% as compared to the flex modulus of the resincomposition without the inclusion of the flex modulus adjusting filler.

A mold release adjusting filler is a filler which allows for the easierremoval of a part from a mold, and eliminates or reduces the need forexternal release agents which otherwise could be applied to the mold. Amold release adjusting filler typically is used in an amount of up toabout 2 wt % based upon the total weight of the layer.

A melt flow index adjusting filler is a filler which increases ordecreases the melt flow, or ease of processing of the composition.

The layers may contain coupling agents that increase adhesion ofmaterials within a particular layer e.g. to couple a filler to a resincomposition, or between adjacent layers. Non-limiting examples ofcoupling agents include titanates, zirconates and silanes. Couplingagents typically are used in amounts of 0.1-2 wt % based upon the totalweight of the composition in which the coupling agent is included.

A density adjusting filler is used to control the moment of inertia, andthus the initial spin rate of the ball and spin decay. The addition inone or more layers, and particularly in the outer cover layer of afiller with a lower specific gravity than the resin composition resultsin a decrease in moment of inertia and a higher initial spin rate thanwould result if no filler were used. The addition in one or more of thecover layers, and particularly in the outer cover layer of a filler witha higher specific gravity than the resin composition, results in anincrease in moment of inertia and a lower initial spin rate. Highspecific gravity fillers are preferred as less volume is used to achievethe desired inner cover total weight. Nonreinforcing fillers are alsopreferred as they have minimal effect on COR. Preferably, the fillerdoes not chemically react with the resin composition to a substantialdegree, although some reaction may occur when, for example, zinc oxideis used in a shell layer which contains some ionomer.

The density-increasing fillers for use in the invention preferably havea specific gravity in the range of 1.0-20. The density-reducing fillersfor use in the invention preferably have a specific gravity of 0.06-1.4,and more preferably 0.06-0.90. The flex modulus increasing fillers havea reinforcing or stiffening effect due to their morphology, theirinteraction with the resin, or their inherent physical properties. Theflex modulus reducing fillers have an opposite effect due to theirrelatively flexible properties compared to the matrix resin. The meltflow index increasing fillers have a flow enhancing effect due to theirrelatively high melt flow versus the matrix. The melt flow indexdecreasing fillers have an opposite effect due to their relatively lowmelt flow index versus the matrix.

Fillers which may be employed in layers other than the outer cover layermay be or are typically in a finely divided form, for example, in a sizegenerally less than about 20 mesh, preferably less than about 100 meshU.S. standard size, except for fibers and flock, which are generallyelongated. Flock and fiber sizes should be small enough to facilitateprocessing. Filler particle size will depend upon desired effect, cost,ease of addition, and dusting considerations. The filler preferably isselected from the group consisting of precipitated hydrated silica,clay, talc, asbestos, glass fibers, aramid fibers, mica, calciummetasilicate, barium sulfate, zinc sulfide, lithopone, silicates,silicon carbide, diatomaceous earth, polyvinyl chloride, carbonates,metals, metal alloys, tungsten carbide, metal oxides, metal stearates,particulate carbonaceous materials, micro balloons, and combinationsthereof. Non-limiting examples of suitable fillers, their densities, andtheir preferred uses are as follows:

TABLE 31 Spec. Grav. Comments Filler Type Precipitated hydrated silica2.0 1, 2 Clay 2.62 1, 2 Talc 2.85 1, 2 Asbestos 2.5 1, 2 Glass fibers2.55 1, 2 Aramid fibers (KEVLAR ®) 1.44 1, 2 Mica 2.8 1, 2 Calciummetasilicate 2.9 1, 2 Barium sulfate 4.6 1, 2 Zinc sulfide 4.1 1, 2Lithopone 4.2-4.3 1, 2 Silicates 2.1 1, 2 Silicon carbide platelets 3.181, 2 Silicon carbide whiskers 3.2 1, 2 Tungsten carbide 15.6 1Diatomaceous earth 2.3 1, 2 Polyvinyl chloride 1.41 1, 2 CarbonatesCalcium carbonate 2.71 1, 2 Magnesium carbonate 2.20 1, 2 Metals andAlloys (powders) Titanium 4.51 1 Tungsten 19.35 1 Aluminum 2.70 1Bismuth 9.78 1 Nickel 8.90 1 Molybdenum 10.2 1 Iron 7.86 1 Steel 7.8-7.91 Lead 11.4 1, 2 Copper 8.94 1 Brass 8.2-8.4 1 Boron 2.34 1 Boroncarbide whiskers 2.52 1, 2 Bronze 8.70-8.74 1 Cobalt 8.92 1 Beryllium1.84 1 Zinc 7.14 1 Tin 7.31 1 Metal Oxides Zinc oxide 5.57 1, 2 Ironoxide 5.1 1, 2 Aluminum oxide 4.0 Titanium oxide 3.9-4.1 1, 2 Magnesiumoxide 3.3-3.5 1, 2 Zirconium oxide 5.73 1, 2 Metal Stearates Zincstearate 1.09 3, 4 Calcium stearate 1.03 3, 4 Barium stearate 1.23 3, 4Lithium stearate 1.01 3, 4 Magnesium stearate 1.03 3, 4 Particulatecarbonaceous materials Graphite 1.5-1.8 1, 2 Carbon black 1.8 1, 2Natural bitumen 1.2-1.4 1, 2 Cotton flock 1.3-1.4 1, 2 Cellulose flock1.15-1.5  1, 2 Leather fiber 1.2-1.4 1, 2 Micro balloons Glass 0.15-1.1 1, 2 Ceramic 0.2-0.7 1, 2 Fly ash 0.6-0.8 1, 2 Coupling Agents AdhesionPromoters Titanates 0.95-1.17 Zirconates 0.92-1.11 Silane 0.95-1.2 COMMENTS: 1 Particularly useful for adjusting density of the coverlayer. 2 Particularly useful for adjusting flex modulus of the coverlayer. 3 Particularly useful for adjusting mold release of the coverlayer. 4 Particularly useful for increasing melt flow index of the coverlayer.

All fillers except for metal stearates would be expected to reduce themelt flow index of the cover layer.

The amount of filler employed is primarily a function of weightrequirements and distribution.

The invention has been described with reference to the preferredembodiment. Obviously, modifications and alterations will occur toothers upon reading and understanding the proceeding detaileddescription. It is intended that the invention be construed as includingall such modifications and alterations insofar as they come within thescope of the appended claims or the equivalents thereof.

1. A golf ball comprising: a solid core formed from materials comprisingat least one polybutadiene and an ethylenically unsaturated carboxylicacid selected from the group consisting of zinc diacrylate, zincacrylate and zinc methacrylate, the solid core having a coefficient ofrestitution of 0.770 or more, a mass ranging from 30 grams to 40 grams,and having a diameter of 1.2 inches to 1.6 inches; an inner cover layermolded on the solid core, the inner cover layer having a thicknessranging from 0.03 inch to 0.07 inch, and comprising a metal fatty acidsalt and a blend of ionomers, the blend of ionomers having at least oneionomer with an acid content by weight of 17% to 25%, and 10% to 100%neutralization of the acids by metal ions selected from the groupconsisting of zinc, sodium and magnesium, the solid core and inner coverlayer forming an inner ball having a coefficient of restitution of 0.790or more, and a diameter of 1.48 inches to 1.66 inches; and an outercover layer molded about the inner ball, the outer cover layercomprising at least one ionomer material, the outer cover layer having athickness ranging from 0.03 inch to 0.06 inch; wherein the golf ball hasa coefficient of restitution of at least 0.770, a dimple pattern havingat least 65% or more surface coverage, and a diameter of 1.680 inches ormore.
 2. The golf ball according to claim 1 wherein the outer coverlayer is composed of a blend of ionomers having at least two ionomerswith an acid content by weight of 17% to 25%, and 10% to 100%neutralization of the acids by metal ions selected from the groupconsisting of zinc, sodium and magnesium.
 3. The golf ball according toclaim 1 wherein the metal fatty acid salt of the inner cover layer is ametal stearate.
 4. The golf ball according to claim 3 wherein the metalstearate is a zinc stearate.